Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type 1, 2"/min; ASTM D638 |
Proto3000 ABSi Fused Deposition Modeling Polymer Description: Stratasys ABSi is an ideal material for conceptual modeling, functional prototyping and direct digital manufacturing. Its strength is superior to standard Stratasys ABS, and the translu.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTWE280 ASA Weatherble ASA profile extrusion gradeThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | >= 37.0 MPa | >= 5370 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 524B General Purpose Polystyrene Polystyrene intended to produce glossy coating by co-extrusion. A specialty recipe provides for drastic reduction of buildup in a die plate and of streaks on an article in molding.Information provi.. |
|||
Tensile Strength at Break | >= 37.0 MPa | >= 5370 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 525 General Purpose Polystyrene Grade 525 is a crystal polystyrene for both injection molding and cap layer co-extrusion. Injection molding applications such as medical and laboratory parts, tumblers, and jewel boxes demonstrate t.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Geloy FXTW26SK ASA (Europe-Africa-Middle East) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride
(discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RH 210/K1 Rigid PVC, Antishock Extrusion Antishock profiles |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RH 225 Rigid PVC, Antishock Extrusion Antishock pipes and profiles |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RK 435 Rigid PVC, Extrusion Lead Free Electrical channels |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
Fainplast Compounds RKS 325/W-UV Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock UV resistant |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KL005 Acetal Copolymer LNP LUBRICOMP* KL005 is a compound based on Acetal Copolymer resin containing 25% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X2420 PC+POLYESTER (Asia Pacific) Xenoy*X2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad co.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer LNP THERMOCOMP* KB005 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® K3501 PBT Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive unde.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy W3000 PBT LNP STAT-LOY* W3000 is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americ.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF MX00619 PP LNP* Thermotuf* MX00619 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
Sumitomo Bakelite North America SI 9550 Silicone Compound SI 9550 is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated tempera.. |
|||
Tensile Strength at Break | 37.0 MPa @Temperature 23.0 °C |
5370 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Crastin® CE2056 NC010 PBT Crastin® CE2056 NC010 is an unreinforced polybutylene terephthalate molding resin.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ASTM D638 |
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 50mm/min; ISO 527-2 |
Denka MALECCA K-600 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM-D638 |
Braskem GM7040G HDPE High Density Extrusion Polyethylene GM7040G is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for a gas pressurized line. It is produced with bimodal technology and has high molar mass.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D412 |
Alliance Polymers Zythane™ 7085AU Thermoplastic Polyurethane Elastomer Zythane™ 7085UF is a UV stabilized polyether-based TPU specifically formulated for extrusion applications. It exhibits excellent abrasion resistance and toughness and has good hydrolytic stability,.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific) LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based .. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
Polimeri Europa Edistir N 1910 Polystyrene Very easy flow general purpose polystyrene. Used for injection of thin-wall, multi-cavity, very fast-cycle mouldings and for sheet extrusion in glossy capping of HIPS and in blend with HIPS or clear.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD4471 PC (Europe-Africa-Middle East) Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||
Tensile Strength at Break | 37.0 MPa | 5370 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retard.. |