SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer (Asia Pacific)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Extem
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Global Food Contact Approval. Resin is subject to Commerce Control Laws U.S. 15CFR Chapter VII, Part 774 and Annex I of Reg. EC 428/2009 as ECCN1C008.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	ASTM D792
Density	1.30 g/cc	0.0470 lb/in³	ISO 1183
Moisture Absorption	0.600 %	0.600 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	1.75 %	1.75 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	on Tensile Bar; SABIC Method
	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	15.5 g/10 min @Load 6.60 kg, Temperature 367 °C	15.5 g/10 min @Load 14.6 lb, Temperature 693 °F	ASTM D1238
Melt Index of Compound	8.0 g/10 min @Load 5.00 kg, Temperature 360 °C	8.0 g/10 min @Load 11.0 lb, Temperature 680 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, H358/30	140 MPa	20300 psi	ISO 2039-1
Tensile Strength at Break	78.0 MPa	11300 psi	5 mm/min; ISO 527
	96.0 MPa	13900 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	95.0 MPa	13800 psi	5 mm/min; ISO 527
	96.0 MPa	13900 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	50 %	50 %	5 mm/min; ISO 527
	50 %	50 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	6.0 %	6.0 %	Type I, 5 mm/min; ASTM D638
	8.5 %	8.5 %	5 mm/min; ISO 527
Tensile Modulus	3.11 GPa	451 ksi	1 mm/min; ISO 527
	3.51 GPa	509 ksi	5 mm/min; ASTM D638
Flexural Strength	159 MPa	23100 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength	123 MPa	17800 psi	2 mm/min; ISO 178
	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus	3.08 GPa	447 ksi	2 mm/min; ISO 178
	3.17 GPa	460 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.690 J/cm	1.29 ft-lb/in	ASTM D256
	0.740 J/cm @Temperature -30.0 °C	1.39 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
Izod Impact, Notched (ISO)	4.00 kJ/m²	1.90 ft-lb/in²	80104; ISO 180/1A
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	80104; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80104; ISO 180/1U
Charpy Impact Unnotched	NB	NB	Edgew 80104 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80104 sp=62mm; ISO 179/1eU
Dart Drop, Total Energy	33.0 J @Temperature 23.0 °C	24.3 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C @Temperature -40.0 - 150 °C	27.8 µin/in-°F @Temperature -40.0 - 302 °F	ASTM E 831
	50.0 µm/m-°C @Temperature 23.0 - 150 °C	27.8 µin/in-°F @Temperature 73.4 - 302 °F	ISO 11359-2
CTE, linear, Transverse to Flow	50.0 µm/m-°C @Temperature -40.0 - 150 °C	27.8 µin/in-°F @Temperature -40.0 - 302 °F	ASTM E 831
	50.0 µm/m-°C @Temperature 23.0 - 150 °C	27.8 µin/in-°F @Temperature 73.4 - 302 °F	ISO 11359-2
Thermal Conductivity	0.220 W/m-K	1.53 BTU-in/hr-ft²-°F	ASTM E 1530
Deflection Temperature at 0.46 MPa (66 psi)	237 °C @Thickness 6.40 mm	459 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	228 °C	442 °F	Flatw 80104 sp=64mm; ISO 75/Af
	217 °C @Thickness 3.20 mm	423 °F @Thickness 0.126 in	unannealed; ASTM D648
	230 °C @Thickness 6.40 mm	446 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	238 °C	460 °F	Rate B/120; ISO 306
	242 °C	468 °F	Rate B/50; ASTM D1525
	242 °C	468 °F	Rate B/50; ISO 306
Glass Transition Temp, Tg	247 °C	477 °F
Oxygen Index	45 %	45 %	ISO 4589
Glow Wire Test	850 °C	1560 °F	IEC 60695-2-13
	960 °C @Thickness 3.20 mm	1760 °F @Thickness 0.126 in	IEC 60695-2-12

Optical Properties	Metric	English	Comments
Haze	2.0 % @Thickness 2.54 mm	2.0 % @Thickness 0.100 in	ASTM D1003
Transmission, Visible	58 %	58 %	2.54 mm; ASTM D1003

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.41 @Frequency 100 Hz	3.41 @Frequency 100 Hz	ASTM D150
	3.41 @Frequency 1000 Hz	3.41 @Frequency 1000 Hz	ASTM D150
Dielectric Strength	17.0 kV/mm @Thickness 3.20 mm	432 kV/in @Thickness 0.126 in	in oil; ASTM D149
Dissipation Factor	0.0010 @Frequency 1000 Hz	0.0010 @Frequency 1000 Hz	IEC 60250
	0.0070 @Frequency 1.00e+6 Hz	0.0070 @Frequency 1.00e+6 Hz	IEC 60250
	0.0080 @Frequency 100 Hz	0.0080 @Frequency 100 Hz	IEC 60250
	0.025 @Frequency 50.0 - 60.0 Hz	0.025 @Frequency 50.0 - 60.0 Hz	IEC 60250
Comparative Tracking Index	175 V	175 V	IEC 60112

Descriptive Properties	Value	Comments
Ball Pressure Test, 125°C +/- 2°C	Passes	IEC 60695-10-2