- SABIC Innovative Plastics Cycoloy® CY6414 PC+ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics Cycoloy® CY6414 PC+ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® CY6414 PC+ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 260 °C |
13 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
| 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 85 % | 85 % | Type I, 50 mm/min; ASTM D 638 |
| >= 100 % | >= 100 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.7 % | 5.7 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.33 GPa | 338 ksi | 5 mm/min; ASTM D 638 |
| 2.42 GPa | 351 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.47 GPa | 358 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.15 J/cm @Temperature -30.0 °C |
4.03 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 5.25 J/cm @Temperature 0.000 °C |
9.84 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 7.95 J/cm @Temperature 23.0 °C |
14.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 14.0 kJ/m² @Temperature 0.000 °C |
6.66 ft-lb/in² @Temperature 32.0 °F |
80*10*3; ISO 180/1A | |
| 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.70 J/cm² @Temperature 0.000 °C |
8.09 ft-lb/in² @Temperature 32.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 2.80 J/cm² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 118 °C @Thickness 6.40 mm |
244 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 133 °C | 271 °F | Rate B/50; ISO 306 |
| 134 °C | 273 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
UL 94 |
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 | |
| Oxygen Index | 32 % | 32 % | LOI; ISO 4589 |
| Glow Wire Test | 775 °C @Thickness 0.750 mm |
1430 °F @Thickness 0.0295 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 775 °C @Thickness 1.50 mm |
1430 °F @Thickness 0.0591 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 775 °C @Thickness 3.00 mm |
1430 °F @Thickness 0.118 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
Glow Wire Flammability Index 960°C, passes at, by VDE; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 4.00e+16 ohm | <= 4.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.94 @Frequency 1.00e+6 Hz |
2.94 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| 3.0 @Frequency 1000 Hz |
3.0 @Frequency 1000 Hz |
ASTM D 150 | |
| Dissipation Factor | 0.0016 @Frequency 1000 Hz |
0.0016 @Frequency 1000 Hz |
ASTM D 150 |
| 0.0088 @Frequency 1.00e+6 Hz |
0.0088 @Frequency 1.00e+6 Hz |
ASTM D 150 | |
| 0.0088 @Frequency 1.00e+6 Hz |
0.0088 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC code 3; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | surface, PLC code 1; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Pass | IEC 60695-10-2 |
| Ball Pressure Test, 125°C +/- 2°C, by VDE | Pass | IEC 60695-10-2 |