SABIC 120W Linear Low Density Polyethylene for Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC 120W Linear Low Density Polyethylene for Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: 120W is a Linear Low Density Polyethylene grade suitable for general purpose packaging. Films produced using this resin yield good tensile properties, impact strength and optical properties.Formulation: 1500 ppm Slip & 3000 ppm AntiblockTypical Applications: Ice & frozen food bags, liners, produce bags, bread bags, textile & garment packaging, etc.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
load density; ASTM D1505
Thickness 30.0 microns
1.18 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.00 MPa
1310 psi
ASTM D882
Film Elongation at Break, MD 650 %
650 %
ASTM D882
Film Elongation at Break, TD 810 %
810 %
ASTM D882
Elmendorf Tear Strength MD 160 g
160 g
ASTM D1922
Elmendorf Tear Strength TD 350 g
350 g
ASTM D1922
Elmendorf Tear Strength, MD 5.33 g/micron
135 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 11.67 g/micron
296.4 g/mil
ASTM D1922
Dart Drop Total Energy 600 J/cm
1.12 ft-lb/mil
Puncture Resistance; SABIC Method
Dart Drop 4.00 g/micron
102 g/mil
ASTM D1709
Dart Drop Test 120 g
0.265 lb
ASTM D1709
Film Tensile Strength at Break, MD 38.0 MPa
5510 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
1% Secant Modulus, MD 260 MPa
37700 psi
ASTM D882
1% Secant Modulus, TD 270 MPa
39200 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 100 °C
212 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 10 %
10 %
ASTM D1003
Gloss 90 %
90 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 195 - 215 °C
383 - 419 °F
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0