Polymer Property : Film Tensile Strength at Break, MD = 38.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex CL 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 106 are characterized by h..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
SABIC 120W Linear Low Density Polyethylene for Blown Film Product Description: 120W is a Linear Low Density Polyethylene grade suitable for general purpose packaging. Films produced using this resin yield good tensile properties, impact strength and opti..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D 882
NOVA Chemicals Novapol® TF-0438-E Hexene LMDPE Film Resin TF-0438-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
NOVA Chemicals Sclair® 19G Homopolymer HDPE Film Resin Features: Excellent barrier propertiesHigh stiffnessGood processability Low gel Applications: Barrier filmsCo-extrusionDry food packagingInformation provided by Nova Chemicals
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Reliance Industries Reclair F18010 Polyethylene Butene comonomer based Linear Low Density Polyethylene blow film grade. Applications:lamination films. Information provided by Reliance Industries
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
NOVA Chemicals Novapol® PF-Y821-B Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Good stiffness and machinability, good clarity with LDPE.Applications: General purpose packaging, liners.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
NOVA Chemicals Novapol® PF-Y821-D Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Good stiffness and machinability, good blocking resistance.Applications: Bags-on-roll, produce bags, garment film, trash bags.Data provided by the manufacturer.
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Reliance Industries Reclair F19010 Polyethylene Blow film Linear Low Density Polyethylene grade. Reclair F19010 is butene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. Th..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 50.8 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.LWS is a linear medium density polyolefin film produced from Sclair® copolymer resin and designed primarily for laminating end uses. It is treated on one..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
DuPont™ Sclairfilm® LWS-2 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.LWS is a linear medium density polyolefin film produced from Sclair® copolymer resin and designed primarily for laminating end uses. It is treated on one..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
DuPont™ Sclairfilm® LWS-2 LMDPE Film, Laminating, 50.8 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.LWS is a linear medium density polyolefin film produced from Sclair® copolymer resin and designed primarily for laminating end uses. It is treated on one..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Borealis Borstar® FB4250T LLDPE for Blown Film Borstar FB4250 is well suited for a wide range of film applications due to its properties. The well balanced mechanical properties will improve the functionality of the films or allow for material ..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Total EVA 1003 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1003 VN 4 is made by a high pressure tubular process. Grade for flexible films with very high transparency and outstanding mechanical properties. Contains an antioxidant.Application examples: ..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Total LLDPE LL 1810 H Linear Low Density Polyethylene - Blown Film LL 1810 H is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most blown film applications.LL 1810 H can be processed at high o..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Total LLDPE LL 1810 Linear Low Density Polyethylene - Blown Film LL 1810 is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most blown film applications.LL 1810 can be processed at high outpu..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Total Lotrene® Q1018N Linear Low Density Polyethylene, Blown Film Lotrene® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Total EVA 1005 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 5 is made by a high pressure tubular process. Grade for films with high transparency and good mechanical properties. Contains an antioxidant.Application examples: Coextrusion, stretch ..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Total Lotrene® Q1018H Linear Low Density Polyethylene, Blown Film Lotrene® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Braskem LF 0720/20 AF LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Heavy duty bags; "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
Braskem LF 0720/21 AF LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); high clarity films; "liners"; general purpose. Information provided by Braskem
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D-882
Bapolene® 152A Polyethylene Film Grade Bapolene 152A is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products...
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D-882
Bapolene® 152B Polyethylene Film Grade Bapolene 152B is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products...
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D-882
Bapolene® 152F Polyethylene Film Grade Bapolene 152F is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products...
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CLH 196 Hexene Copolymer Linear Low Density Polyethylene Clearflex H&T CLH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Stretch films manufactured with Clearflex H&T CLH 196 have..
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882
DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **) Data provided by DuPont Packaging Polymers.LWS is a linear medium density polyolefin film produced from Sclair® copolymer resin and designed primarily for laminating end uses. It is treated on one..