Sax Polymers SAXAMID 126F4RZ21 Nylon 6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F4RZ21 Nylon 6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F4RZ21 is a polyamide 6 injection-molding-grade reinforced with 20% glass fibers. It is equipped with a halogen-free and phosphorus-free flame retardant.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 124 MPa | 18000 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 8.10 GPa | 1170 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 208 MPa | 30200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² @Temperature -30.0 °C |
31.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 68.0 kJ/m² @Temperature 23.0 °C |
32.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 7.90 J/cm² @Temperature -30.0 °C |
37.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.30 J/cm² @Temperature 23.0 °C |
39.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 216 °C | 421 °F | B/120; ISO 306 |
| Flammability, UL94 | V-2 | V-2 | |
| Glow Wire Test | 600 °C @Thickness 2.00 mm |
1110 °F @Thickness 0.0787 in |
GWFI; IEC 60695-2-12 |
| 725 °C @Thickness 1.00 mm |
1340 °F @Thickness 0.0394 in |
GWIT; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD921A PC (Europe-Africa-Middle East)
- Karina E TR-600N39/381-Y Pink PVC Compound
- Huntsman IROGRAN® A 95 K 6977 TPU-For Seals
- LG Chemical HIPS 65IHE PS, Impact Modified
- Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, Conditioned
- Borealis Borecene™ RM8342RC Linear Polyethylene for Rotational Molding
- 3A Composites Core Materials AIREX® PXc.420 Fiber-Reinforced Structural Foam
- Solvay Specialty Polymers Algoflon® E2 PTFE (Polytetrafluoroethylene) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved