Polymer Property : Film Tensile Strength at Break, TD = 30.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ISO 527-3
Polimeri Europa Clearflex® CL 508 Octene Copolymer Linear Medium Density Polyethylene Clearflex CL 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 508 exhibit a good bal..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ISO 527-3
Polimeri Europa Greenflex® FC 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FC 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FC 45 exhibit good optical properties, excellent impact resistance and low creep..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ISO 527
Premix Thermoplastics PRE-ELEC® ABS 1410 PRE-ELEC ABS 1410 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ABS 141..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
NOVA Chemicals Novapol® TF-0219-E Hexene LLDPE Film Resin Exceptional toughens, Low gel levelApplications: Cast stretch wrapAdditives: High temperature A/OFilm properties are typical of cast film extruded at a melt temperature of 540°F, and a line speed o..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
SABIC HP0322N Low Density Polyethylene for Blown Film Product Description: HP0322N is a Low Density Polyethylene grade suitable for producing heavy duty films and contains no slip or antiblock additives. It yields outstanding toughness and optical pr..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ISO 527
Total Finathene® LL 4010 FH 18 LLDPE film (discontinued **) Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Iran Petrochemical (PCC) Arak 20075AA LLDPE (discontinued **) Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Reliance Industries Reclair F19010 Polyethylene Blow film Linear Low Density Polyethylene grade. Reclair F19010 is butene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. Th..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating (discontinued **) Surlyn® 1652-1 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylen..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Iran Petrochemical (PCC) LL22501 Linear Low Density Polyethylene 22501 is a high stiffness LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels a..
Film Tensile Strength at Break, TD	30.0 - 45.0 MPa	4350 - 6530 psi	50% RH; DIN 53455
Stanelco BioplastÂ® GS 2189 Biodegradable Plastic Bioplast 2189 is a product that is optimised for sheet extrusion, injection and compression moulding. It is always biodegradable and readily compostable in thin sections, this material is useable i..
Film Tensile Strength at Break, TD	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527-3
Borealis BA11CF Polypropylene Copolymer BA110CF is a heterophasic copolymer. This grade is suitable for use on chill roll processes. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. ..
Film Tensile Strength at Break, TD	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527-3
Borealis BD212CF Polypropylene Copolymer BD212CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BD212CF is designed for food packaging, l..
Film Tensile Strength at Break, TD	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527-3
Borealis Bormod™ HD915CF Polypropylene Homopolymer for Cast Film Bormod HD915CF is a high crystallinity homopolymer film resin, based on special Borstar nucleating technology, especially developed for the manufacturing of unoriented film for metallizing. It is s..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	Cast Film at 1 mil; ASTM D-882
Chevron Phillips MarFlex® 7114 Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for applications that require: Good stiffness at thin gaugesGood drawdownExcellent processabilityCan use straight or in blends with L..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem BF 0323 HC LDPE Blown Film Extrusion Polyethylene Description: BF0323HC is a high molecular weight grade produced under high pressure. Films obtained with this product show excellent mechanical and optical properties38µm film gauge, obtained in 75..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem Flexus® 7200 Cast Film Extrusion Polyethylene Description: Braskem Flexus7200 is a Linear Low Density Polyethylene, metallocene ethylene-hexene copolymer, produced by gas fase process. It was specially designed to provide outstanding processing..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem Green PE SLL218/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Line..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem Green PE SLL318 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem LHB 118/21 AF LLDPE Blown Film Extrusion Polyethylene Description: LHB118/21 AF is a LLDPE copolymer produced by Braskem. It is a ready-to-use product since it contains 10% LDPE. Its additive package was optimized to avoid blocking, even at low thickne..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	Ultimate; ASTM D882
Braskem LL118 Blown Film Extrusion Linear Low Density Polyethylene Description: LL218/21 is a LLDPE Butene copolymer produced by Braskem. It was specially designed to provide outstanding processing performance. Films obtained with this grade show good physical and ..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM-D882
Braskem LL318 LLDPE Linear Low Density Extrusion Polyethylene LL318 is a linear low-density polyethylene, copolymer of butene-1, produced by the Spherilene process. It was developed for cast film extrusion. Films obtained with this product show good mechanical..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM-D882
Braskem LL6901S LLDPE Blown Film Extrusion Polyethylene Copolymer LL6901S is a LLDPE Butene copolymer produced by Braskem. It is a ready to use product since it's been compounded with 15% LDPE. It is a general purpose product that shows a good processing performan..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
DuPont™ Surlyn® 2601 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 2601 is an ionomer resin available for use in blown and cast film operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resins. Applicati..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CLH 196 Hexene Copolymer Linear Low Density Polyethylene Clearflex H&T CLH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Stretch films manufactured with Clearflex H&T CLH 196 have..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
NOVA Chemicals Sclair® 11E1 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, strength and toughness.Applications: Base resin.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
ExxonMobil Exceed™ 2018EB Blown Film Resin (discontinued **) Exceed 2018EB resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals Exxpol® Technology. The higher melt index makes this polymer ideally sui..
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem BF0323HC Blown Film Extrusion Low Density Polyethylene Heavy-duty bags; Agriculture, Coextruded and shrink films for pallets.Information provided by Braskem.
Film Tensile Strength at Break, TD	30.0 MPa	4350 psi	ASTM D882
Braskem LF0720/20AF Blown Film Extrusion Linear Low Density Polyethylene Description: LF0720/21AF is a LLDPE Butene copolymer produced using Unipol process technology. It shows excellent optical properties associated with good balance of mechanical properties, processing..