Premix Thermoplastics PRE-ELEC® PE 1304  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , LLDPE
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PE 1304  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC PE 1304 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 1304 has excellent mechanical properties and is suitable for film blowing.Typical applications include blown film for the production of bags for electronic components and other products sensitive to static electricity.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
Thickness 406 microns
16.0 mil
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
1.5 g/10 min

@Load 5.00 kg,
Temperature 190 °C
1.5 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 15.0 MPa
2180 psi
ISO 527
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527
Film Elongation at Break, MD 540 %
540 %
ISO 527
Film Elongation at Break, TD 540 %
540 %
ISO 527
Film Elongation at Yield, MD 15 %
15 %
ISO 527
Film Elongation at Yield, TD 9.0 %
9.0 %
ISO 527
Film Tensile Strength at Break, MD 22.0 MPa
3190 psi
ISO 527
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ISO 527
Electrical Properties Metric English Comments
Surface Resistance <= 1e+05
<= 1e+05
ISO D-257
Processing Properties Metric English Comments
Melt Temperature 160 - 200 °C
320 - 392 °F
Blow-up Ratio (BUR) >= 180
>= 180
Drying Temperature 90.0 °C

@Time 10800 sec
194 °F

@Time 3.00 hour
If stored for longer than 1 year
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Black
Screen Pack As coarse as possible