Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 30 Low Density Polyethylene - Blown Film Extrusion Riblene FF 30 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 30 is characterized by a good melt strength leading to a good bubble stabilit.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 33 Low Density Polyethylene - Blown Film Extrusion Riblene FF 33 is a high molecular weight low density polyethylene (LDPE), with added slip agent, ideal for blown film extrusion. Riblene FF 33 is characterized by a good melt strength leading to a .. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 34 Low Density Polyethylene - Blown Film Extrusion Riblene FF 34 is a high molecular weight low density polyethylene (LDPE), with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FF 34 is characterized by a good melt s.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Polimeri Europa Riblene® FF 39 Low Density Polyethylene - Blown Film Extrusion Riblene FF 39 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 39 is characterized by a good melt strength leading to a good bubble stabilit.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa @Thickness 0.400 mm |
3190 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PS 1324 PRE-ELEC PS 1324 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC .. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1304
(discontinued **) PRE-ELEC PE 1304 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
Huntsman PE 1008 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: industrial packaging, frozen food, produce bags, shrink, a.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
ExxonMobil Escorene® LD-141 EVA Shrink Film Resin, FMI
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A fractional melt index, 2.0% vinyl acetate copolymer film resin with very good toughness and shrink properties. The low melt index gives excellent.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO R527-1 |
Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene LDPE 2101TN47 Shrink FilmThis grade enables high speed production of film without blocking.Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
SCG Chemicals EL-Leneâ„¢ L2020F Linear Low Density Polyethylene Film Key Characteristics:High output and elongationContains 1800 ppm slip agent and 1400 ppm antiblocking agentRecommended Applications:General purpose bag, cast film, small bag, merchandise bag, printed.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Borealis Himod™ FT7293 LDPE for Film Himod FT7293 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Borealis Himod™ FT7294 LDPE for Film Himod FT7294 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Total LDPE 1022 FH 24 Low Density Polyethylene - Blown Film LDPE 1022 FH 24 is a low density polyethylene made by a high pressure process.LDPE 1022 FH 24 is a slip and anti-block formulated grade.LDPE 1022 FH 24 is suited to many applications in the field of.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
Braskem BC 818 LDPE Extrusion Coating Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Extrusion coating. Information provided by Braskem |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
Braskem CX7020 Cast Film Extrusion Low Density Polyethylene Smooth or embossed films for diapers, disposable sheets, etc. Films for lamination, Injection-Blow Molding, Foamed applications.Information provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM-D882 |
Braskem CX7020 LDPE Cast Film Extrusion Polyethylene CX7020 is a low-density polyethylene (LDPE) with excellent processability and low gel content. Those features allow for production of thin and highly uniform films. This product is identified as PE .. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 |
Braskem PB681/59 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Lamination film; general purpose. Information provided by Braskem |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 1184 |
Carmel Olefins IPETHENE® 100 Low Density Polyethylene IPETHENE® 100 is a low density polyethylene extrusion grade. It exhibits good impact and puncture resistance, good processability and good ESCR. APPLICATIONS IPETHENE® 100 is used for production.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 1184 |
Carmel Olefins IPETHENE® 320 Low Density Polyethylene IPETHENE® 320 is a general purpose low density polyethylene film extrusion grade, containing no additives. It exhibits good mechanical and optical properties. APPLICATIONS IPETHENE® 320 is mainl.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 1184 |
Carmel Olefins IPETHENE® 322 Low Density Polyethylene IPETHENE® 322 is a general purpose low density polyethylene film extrusion grade. It contains a medium level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between .. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 1184 |
Carmel Olefins IPETHENE® 323 Low Density Polyethylene IPETHENE® 323 is a general purpose low density polyethylene film extrusion grade. It contains a high level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between me.. |
|||
Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film LDPE 1022 FN 24 is a low density polyethylene made by a high pressure process without antioxidant.LDPE 1022 FN 24 is suited to many applications in the field of consumer, industrial, food or hygiene.. |