Nilit Nilamid B3 H ZC Unfilled, Low Temperature Impact Resistant PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Nilit
Trade Name Nilamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Nilamid B3 H ZC Unfilled, Low Temperature Impact Resistant PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Nilamid B3 H ZC has outstanding impact performance, even at minus temperatures. It is widely used for components subjected to high shock loads. Applications include bicycle components, garden equipment, components in the car interior and industrial machine components.Key characteristics: Outstanding impact strength, even at minus temperaturesHigh elongationEasy processingGood surface finish Information provided by NILIT.
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792, ISO 1183
Water Absorption 2.0 %
2.0 %
23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 8.0 %
8.0 %
sim. ISO 62
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
Euronil
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
Euronil
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527, ASTM D638
Elongation at Yield >= 100 %
>= 100 %
ISO 527, ASTM D638
Flexural Yield Strength 75.0 MPa
10900 psi
ISO 178, ASTM D790
Flexural Modulus 1.70 GPa
247 ksi
ISO 178, ASTM D790
Izod Impact, Notched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179
2.20 J/cm²

@Temperature -30.0 °C
 10.5 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75, ASTM D648
Vicat Softening Point 174 °C
345 °F
49 N; ISO 306, ASTM D1525
208 °C
406 °F
9.8 N; ISO 306, ASTM D1525
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Dielectric Strength 19.0 kV/mm

@Thickness 2.00 mm
 483 kV/in

@Thickness 0.0787 in
 ASTM D149
Comparative Tracking Index 550 V

@Thickness 3.20 mm
 550 V

@Thickness 0.126 in
 Sol. B; IEC 112, UL 746A
600 V

@Thickness 3.20 mm
 600 V

@Thickness 0.126 in
 Sol. A; IEC 112, UL 746A
Processing Properties Metric English Comments
Nozzle Temperature 240 - 270 °C
464 - 518 °F
Zone 1 230 - 260 °C
446 - 500 °F
hopper
Zone 2 230 - 260 °C
446 - 500 °F
Zone 3 240 - 270 °C
464 - 518 °F
Zone 4 240 - 270 °C
464 - 518 °F
Melt Temperature 240 - 280 °C
464 - 536 °F
Do not melt above 300°C
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80°C is Preferred
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 4 hour
4 hour
Injection Pressure 70.0 - 100 MPa
10200 - 14500 psi
Descriptive Properties Value Comments
Clamping Force in tons, 0.7 times the projected surface area in cm2
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309
Holding Pressure 90 MPa