Polymer Property : Film Tensile Strength at Yield, TD = 1890 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527-3
Polimeri Europa Clearflex® FG 306 Hexene Copolymer Linear Low Density Polyethylene
Clearflex FG 306 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidant, antiblocking and processing aid, suitable for blown film extrusion.Films manufactured with Clearf..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527-3
Polimeri Europa Clearflex® FG 336 Hexene Copolymer Linear Low Density Polyethylene
Clearflex FG 336 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidant, slip agent, antiblocking agent and processing aid, suitable for blown film extrusion.Films obtain..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
SABIC 6821N Linear Low Density Polyethylene for Blown Film
Product Description: 6821N is a fractional melt index hexene copolymer based Linear Low Density Polyethylene grade suitable for high strength packaging applications. Films produced using this resi..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527-3
Polimeri Europa Flexirene® FG 30 Butene Copolymer Linear Low Density Polyethylene
Flexirene FG 30 is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Flexirene FG 30 are characterized by an..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527-3
Polimeri Europa Flexirene® FG 30 U Butene Copolymer Linear Low Density Polyethylene
Flexirene FG 30 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Flexirene FG 30 U are characterized b..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527
Premix Thermoplastics PRE-ELEC® CP 1319
PRE-ELEC CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1319 ..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
2 in per min; ASTM D882
Chevron Phillips Marlex® D252/257 Linear Low Density Polyethylene Film Resin  (discontinued **)
Low Density, Linear Polyethylene Film ResinCustomer Benefits: This unique broad molecular weight distribution resin has a wide processing window and produces film with an excellent combination of to..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.An LLDPE blown film resin. Films made from LL-1117 have very good tensile properties and toughness. This resin's good strength and drawability all..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
Iran Petrochemical (PCC) Arak 0410AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO 527
Premix Thermoplastics PRE-ELEC® PE 1304  (discontinued **)
PRE-ELEC PE 1304 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
Reliance Industries Reclair O19010 Polyethylene
Blow film Linear Low Density Polyethylene grade. Reclair O19010 is octene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. Th..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882
Reliance Industries Reclair O21010 Polyethylene
Octene comonomer based Linear Low Density Polyethylene. Blow film grade. Contains an optimum level of antioxidants and polymer processing aids. Designed for lamination film applications. Character..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882-02
Ipiranga Petrochem LB 0117 LLDP
IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM D882-02
Ipiranga Petrochem LB 0120 BS LLDP
IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ISO R527-1
Iran Petrochemical (PCC) 2404TC47 Low Density Polyethylene
LDPE 2404TC47 Light duty FilmIt is used for very thin films requiring good optical properties for general packaging applications e.g. covering film with very low blocking tendency.Information provi..
Film Tensile Strength at Yield, TD 13.0 MPa
1890 psi
ASTM-D882
Braskem Symbios 4102 Polypropylene Terpolymer
Braskem Symbios 4102 is a medium melt flow rate terpolymer with a heat seal temperature below 120ºC on its treated face. It is designed for use as a heat sealing layer on bioriented films (BOPP) an..
Film Tensile Strength at Yield, TD >= 13.0 MPa
>= 1890 psi
Iran Petrochemical (PCC) Tabriz 0410AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.