Polykemi AB POLYfill PPC T8020 FC Polypropylene Copolymer, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 20% Talc Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYfill PPC T8020 FC Polypropylene Copolymer, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Filler Content | 23 % | 23 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | With Flow; ISO 2577 |
| 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 29.0 MPa | <= 4210 psi | ISO/R527 |
| Elongation at Break | 22 % | 22 % | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 49.0 MPa | <= 7110 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 2.10 J/cm² @Temperature -20.0 °C |
9.99 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 4.10 J/cm² @Temperature 23.0 °C |
19.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 58.0 °C @Load 5.001 kg |
136 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 140 °C @Load 1.00 kg |
284 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Mytex Polymers AS65KW-1ATM Polypropylene, Talc filled, Compounded
- LNP NORYL® EXCP0111 PPS + Polyphenylene Ether, 42% Glass / Mineral Reinforcement (discontinued **)
- Nye Lubricants 774F (NG) Synthetic Oil
- Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick
- Lanxess Durethan® BKV 30 H2.0 901510 Nylon 6, 30% Glass Fiber
- SABIC Innovative Plastics SABIC PPCOMPOUND 8620A PP
- Polyram PlusTek PB140 Nylon 6, Injection Molding
- Hexcel® HexWeb® HRH-10 - 1/4 - 3.1 Aramid Fiber/Phenolic Resin Honeycomb
- Eastman Drystar 0113 Copolyester
- Carlson C 600 Nickel-Chromium-Iron Alloy
Copyright © lookpolymers.com All Rights Reserved