- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 112 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 112 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC T12020 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics GELOY XP4034 ASA+PC (Europe-Africa-Middle East) GELOY XP4034 is a high heat modified ASA+PC alloy. It is a weatherable, injection mouldable product which is available in a wide range of colours. The product is recommended for automotive unpainted.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75 |
| Solvay Engineered Polymers SEQUEL® 2300 Engineered Polyolefin
(discontinued **) Description: SEQUEL® 2300 engineered polyolefin is designed for large mold-in-color automotive interior applications that require high stiffness and dimensional stability over a broad temperature r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9110 10% Talc-Filled Polypropylene Block-Copolymer INNOPOL® CS 2-9110 is a 10% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9110 is developed for producing.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical XR409E ABS, Heat Resistance Feature: Injection Molding, Heat ResistanceApplication: Automotives Interior Housing (Switch Panel Housing etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Ch.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa MAC-451PG Electroplating PC/ABS Alloy Features:Excellent balance propertiesGood impact strengthGood processing propertiesSuit for electro-platingApplications:Injection moldingAutomobile license plateWater tank coverComputer and accessor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | Unannealed; ISO 75B-1, -2 |
| LyondellBasell Hostacomâ„¢ CB275FC Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB275FC high melt flow, 1,900 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS E GM15 LE 15% Glass Filled Availability: North AmericaFeatures: Low ExtractablesForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS E GM5 LE 5% Glass Filled Availability: North AmericaFeatures: Low ExtractablesForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 5% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS GF20 IM 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedTPCI# 7782121Information provided by T.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS GF30 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS GF40 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP MB006S PP LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl INT1000 PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 6.40 mm |
234 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PN235 PPE+PS (Asia Pacific) Plating grade, primarily automotive applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP (Asia Pacific) PPE+PP blend. Suitable for painted exterior automotive applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS GF30 IM 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedInformation provided by TP Composites,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® ABS IM TM20 20% Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 20% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedProcessing Method: Injection MoldingInformation p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-2 |
| Borealis Daplen™ MD206U Polypropylene Compound 20% Mineral Filled Daplen MD206U is a 20% mineral filled polypropylene compound intended for injection molding. MD206U has been developed especially for automotive interior parts that require excellent balance betwee.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene DescriptionPolyfort® E-15937B is a high strength impact modified polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| A. Schulman PP 1621 Polypropylene Low Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1621 is a low flow homopolymer polypropylene primarily used for sheet strapping and profile extrusion applications.ApplicationPP 1621 meets FDA Regulation 21 CFR 177.1520.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ISO 75-1/-2 |
| Covestro Bayblend® T45 Polycarbonate + ABS General purpose injection molding gradeVicat/B 120 temperature = 112 °CPreprocessingMax. Water content |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | LAB036 |
| ExxonMobil Mytex™ AS23K(W)-01 Talc filled compounded polypropylene produced for automotive interior applicationsInformation provided by ExxonMobil Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 233 °F | ASTM D648 |
| ExxonMobil PP1572 Polypropylene Homopolymer Product Description: A nucleated homopolymer resin designed for general-purpose compression molding of articles such as caps and closures. It exhibits excellent strength and high crystallization te.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Cheng Yu Plastic A708G3 SAN, 30% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 - 140 °C | 234 - 284 °F | ASTM D648 |
| Arkema Group KYNAR® 460 Polyvinylidene Fluoride Homopolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Broad molecular weight distribution. High stability in harsh thermal, chemical and ultraviolet environments. High toughness a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC K8040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| BP Amoco Acctuf® 3240 Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Extrusion; Fiber Optic CableFeatures: NucleatedComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples. |
|||