PolyOne Trilliant™ HC HC3620-0040 RS Natural Polycarbonate + PBT (PC+PBT)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer PolyOne Corporation
Trade Name Trilliant™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Trilliant™ HC HC3620-0040 RS Natural Polycarbonate + PBT (PC+PBT).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead of the competition. When specified, Trilliant® compounds may incorporate agency rated materials that meet USP Class VI, FDA or ISO 10993 testing requirements.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0070 cm/cm
0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 43.4 MPa
6290 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 100 %
100 %
Type I, 51 mm/min; ASTM D638
Flexural Strength 59.3 MPa
8600 psi
ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
ASTM D790
Izod Impact, Notched 6.90 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
12.9 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Melting Point 249 - 271 °C
480 - 520 °F
Deflection Temperature at 0.46 MPa (66 psi) >= 80.0 °C

@Thickness 3.18 mm
>= 176 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 37.8 - 60.0 °C
100 - 140 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 3.00 hour
3.00 hour
Descriptive Properties Value Comments
Agency Ratings USP Class VI
Appearance Natural Color
Features Biocompatible
Good Chemical Resistance
Good Colorability
High Impact Resistance
Specialty Grade
Forms Pellets
Generic Material PC+PBT
Generic Name Polycarbonate + PBT (PC+PBT)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Hospital Goods
Housings
Medical Appliances
Medical/Healthcare Applications