LyondellBasell Petrothene® NA963083 Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® NA963083 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ApplicationsPETROTHENE NA 963 is a series of resins formulated with special antiblock additive and designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA 963 exhibits uniformity, ease of processing and good tensile strength. Regulatory StatusThe basic resin NA 963 meets the requirements of the Food and Drug Administration regulation, 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "…articles or components of articles intended for use in contact with food…" Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information. Processing TechniquesGenerally recommended extrusion conditions include a melt temperature range of 310°350°F; a blow-up ratio range of 1.8-2.5:1. Drawdown to 1.0 mils is possible at commercial rates when proper extrusion techniques are used. Specific recommendations for processing NA 963 can be made only when the end use applications, required properties and processing equipment are known. For exact recommendations, contact your Equistar sales representative. Physical PropertiesThese are typical values and not to be construed as specific product limits. Data obtained from film produced in a 3.5" (98 mm)blown film line, commercially available 8"(203 mm) die, 350°F(177°C) melt extrusion temperature, 2:1 BUR, 1.25 mil(32 micron)gauge, 0.025" die gap at 150 lb/hr.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 31.8 microns
1.25 mil
2:1 BUR; 25 mil die gap
Melt Flow 0.70 g/10 min
0.70 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 46
46
Molded; ASTM D2240
Tensile Strength at Break 11.4 MPa
1650 psi
Molded; ASTM D638
Tensile Strength, Yield 10.7 MPa
1550 psi
Molded; ASTM D638
Film Elongation at Break, MD 160 %
160 %
ASTM D882
Film Elongation at Break, TD 480 %
480 %
ASTM D882
Elongation at Break 700 %
700 %
Molded; ASTM D638
Elongation at Yield 100 %
100 %
Molded; ASTM D638
Elmendorf Tear Strength MD 300 g
300 g
ASTM D1922
Elmendorf Tear Strength TD 180 g
180 g
ASTM D1922
Dart Drop Test 130 g
0.287 lb
F<sub>50</sub>; ASTM D1709
Film Tensile Strength at Break, MD 23.4 MPa
3400 psi
ASTM D882
Film Tensile Strength at Break, TD 16.5 MPa
2400 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 221 MPa
32000 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 90.0 °C
194 °F
ASTM D1525
Brittleness Temperature -75.0 °C
-103 °F
Molded; F<sub>50</sub>; ASTM D746
Processing Properties Metric English Comments
Melt Temperature 177 °C
350 °F