PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with PTFE Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ SF-000/40T Polyphenylene Sulfide - 40% PTFE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.582 g/cc
0.05715 lb/in³
ASTM D792
Water Absorption 0.10 %
0.10 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.010 - 0.020 cm/cm

@Thickness 3.17 mm
 0.010 - 0.020 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 38.0 MPa
5510 psi
ASTM D638
Elongation at Break 1.0 - 4.0 %
1.0 - 4.0 %
ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 0.270 - 0.370 J/cm

@Thickness 6.35 mm
 0.506 - 0.693 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 177 °C
351 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ASTM D648
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 601 °F
Stock
Mold Temperature 135 - 149 °C
275 - 300 °F
Drying Temperature 149 °C
300 °F