PolyOne Lubri-Tech™ PI-000/15T Polyetherimide (PEI), PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ PI-000/15T Polyetherimide (PEI), PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:PTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.354 g/cc | 1.354 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 113 g/10 min @Load 2.16 kg, Temperature 190 °C |
113 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A - Manual Operation; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | Annealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 371 °C | 600 - 700 °F | Molding |
| Mold Temperature | 121 - 177 °C | 250 - 350 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® MQ 10 R Low Density Polyethylene - Injection Molding
- PTS PCA-2010NH Non-Bromine, Non-Chlorine, Flame Retardant PC/ABS Alloy
- Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes
- Styron CALIBREâ„¢ 303 EP Polycarbonate
- SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific)
- Borealis HG385MO Polypropylene
- Arlon 18646B026 0.026" (0.66 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ TFM™ 1700 Modified PTFE Powder
- Victrex® PEEK 450CA20 Polyetheretherketone, 20% Carbon Fibre Reinforced
Copyright © lookpolymers.com All Rights Reserved