PlastiComp Complet® LGF60 - PP Homopolymer Polypropylene, 60% Long Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 60% Glass Fiber Filler
Manufacturer PlastiComp
Trade Name Complēt®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PlastiComp Complet® LGF60 - PP Homopolymer Polypropylene, 60% Long Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 60% long glass fiber reinforcementInformation provided by PlastiComp, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.48 g/cc
1.48 g/cc
ASTM D-792
Filler Content 60 %
60 %
Long Glass Fiber
Mechanical Properties Metric English Comments
Tensile Strength 117 MPa
17000 psi
ASTM D-638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D-638
Tensile Modulus 11.034 GPa
1600.3 ksi
ASTM D-638
Flexural Strength 186 MPa
27000 psi
ASTM D-790
Flexural Modulus 10.345 GPa
1500.4 ksi
ASTM D-790
Izod Impact, Notched 3.42 J/cm
6.41 ft-lb/in
ASTM D-256
Izod Impact, Unnotched 6.94 J/cm
13.0 ft-lb/in
ASTM D-4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 153 °C
307 °F
ASTM D-648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 210 °C
390 - 410 °F
Middle Barrel Temperature 204 - 216 °C
400 - 420 °F
Front Barrel Temperature 210 - 221 °C
410 - 430 °F
Nozzle Temperature 204 - 216 °C
400 - 420 °F
Melt Temperature 210 - 221 °C
410 - 430 °F
Mold Temperature 79.4 °C
175 °F
Injection Velocity 50.8 - 76.2 mm/sec
2.00 - 3.00 in/sec
Drying Temperature 93.0 °C

@Time 7200 sec
199 °F

@Time 2.00 hour
Back Pressure 0.172 - 0.345 MPa
25.0 - 50.0 psi
Cushion 0.635 cm
0.250 in
Screw Speed 30 - 50 rpm
30 - 50 rpm
Descriptive Properties Value Comments
Injection Pressure Medium to maximum