Plastcom SLOVAMID 6 HI-M PA6 with improved impact strength

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Plastcom spol. s r.o.
Trade Name	SLOVAMID
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom SLOVAMID 6 HI-M PA6 with improved impact strength.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6 with the content of thermoplastic elastomer. Impacted, for moldings with higher toughness even at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets, protection ledges of the car-doors. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³	STN EN ISO 1183-1
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	STN EN ISO 527-2
Elongation at Break	4.0 %	4.0 %	STN EN ISO 527-2
Tensile Modulus	1.45 GPa	210 ksi	STN EN ISO 527-2
Flexural Strength	60.0 MPa	8700 psi	STN EN ISO 178
Flexural Modulus	1.20 GPa	174 ksi	STN EN ISO 178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	STN EN ISO 179
	NB @Temperature -20.0 °C	NB @Temperature -4.00 °F	STN EN ISO 179
Charpy Impact, Notched	1.60 J/cm² @Temperature -20.0 °C	7.61 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	2.10 J/cm² @Temperature 23.0 °C	9.99 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi)	58.0 °C	136 °F	STN EN ISO 75-2 (A)
Vicat Softening Point	188 °C	370 °F	STN EN ISO 306
Flammability, UL94	HB	HB
Glow Wire Test	650 °C @Thickness 3.00 mm	1200 °F @Thickness 0.118 in	STN EN 60695-2-12

Processing Properties	Metric	English	Comments
Melt Temperature	240 - 260 °C	464 - 500 °F
Mold Temperature	50.0 - 60.0 °C	122 - 140 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.15 %	0.15 %	STN EN ISO 3344
Injection Pressure	80.0 - 150 MPa	11600 - 21800 psi

Users viewing this material also viewed the following: