- PolyOne Edgetek® PI-20GM/000 L Polyetherimide (PEI), Glass Filled (discontinued **)
PolyOne Edgetek® PI-20GM/000 L Polyetherimide (PEI), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PI-20GM/000 L Polyetherimide (PEI), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Milled Glass Fiber ReinforcedHigh FlowPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.17 mm |
0.20 % @Thickness 0.125 in |
24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 - 6.0 % | 5.0 - 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 4.34 GPa | 630 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.900 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 343 - 371 °C | 650 - 700 °F | Molding |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E80H Ethylene Propylene Rubber
- Osprey Metals Co502 Cobalt Alloy Powder (Grade 95% - 16)
- Taiwan Sheen Soon Sheenthane® A7810H TPU for Ink
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA
- Dow Corning SILASTIC® 9252/250P PARTS A&B
- Covestro Makrolon® 3158 Polycarbonate
- Diamond Polymers ABS 3501ELG High Impact, Low Gloss
- Arlon 51268R015P 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved