NOVA Chemicals Novapol® 20% LF-0718-A in PF-0118-B LDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Novapol®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Novapol® 20% LF-0718-A in PF-0118-B LDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical of blown film extruded at a blowup ratio of 2.5:1, but are dependent upon operating conditions.Information provided by NOVA Chemicals.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 12.0 MPa
1740 psi
ASTM D882
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.180 GPa
26.1 ksi
at 1%; ASTM D882
Secant Modulus, TD 0.240 GPa
34.8 ksi
at 1%; ASTM D882
Impact 50
50
J/mm; NOVA Chemicals Puncture test
Coefficient of Friction <= 0.20
<= 0.20
ASTM D1894
Elmendorf Tear Strength, MD 1.20 g/micron
30.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 15.7 g/micron
399 g/mil
ASTM D1922
Dart Drop 2.20 g/micron
55.9 g/mil
F<sub>50</sub>, ASTM D1709/A
Film Tensile Strength at Break, MD 33.0 MPa
4790 psi
ASTM D882
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ASTM D882
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 60 %
60 %
at 45°; ASTM D2457
Descriptive Properties Value Comments
Blow Up Ratio 2:1 to 3:1