BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 |
| Water Absorption | 2.2 % | 2.2 % | 24 hour; ISO Test |
| 6.6 % | 6.6 % | beginning dry; ISO 62 | |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 160 cm³/g | 160 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 0.2 in/min; ASTM Test |
| Tensile Modulus | 5.00 GPa | 725 ksi | ASTM Test |
| Izod Impact, Notched | 1.34 J/cm @Thickness 3.17 mm |
2.51 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK23220 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Nyco M1250 AS WOLLASTOCOAT® Wollastonite
- ICO Polymers ICOFLOâ„¢ 510-5059 500 Micron LDPE Powder
- Karina BT-0002/17 White PVC Compound
- Toyobo T-750 Nylon, Painting Grade
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N330 (HAF) Filler
- Engineered Polymer Solutions PBT VM 450, 20% Mineral Filled
- Arlon Thermavac® 0.020" (0.508 mm) Uncured Silicone Vacuum Bagging (30400R020)
- Axiall 7751 Rigid PVC, Extrusion
- AK Steel 439 LT Ferritic Stainless steel
Copyright © lookpolymers.com All Rights Reserved