Polymer Property : Film Tensile Strength at Break, MD = 33.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
SABIC 6318B Linear Low Density Polyethylene for Cast Film Product Description: 6318B is a hexene copolymer Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high process..
Film Tensile Strength at Break, MD	33.0 MPa @Thickness 0.400 mm	4790 psi @Thickness 0.0157 in	ISO 527
Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound PRE-ELEC® PP 1396 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
NOVA Chemicals Novapol® 20% LF-0718-A in PF-0118-B LDPE Film Resin Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical ..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin Features: Exceptional toughnessLow gel level Applications: Cast stretch wrapNettingCo-extrusion and laminationInformation provided by Nova Chemicals
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman 1810F Polyethylene (discontinued **) Polyethylene 1810F is a fractional-melt low-density formulation with no slip or antiblock. It is suggested for film applications requiring high impact strength, high tear strength and very good opt..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman D4004-F Polyethylene (discontinued **) Polyethylene D4004-F is a fractional melt formulation designed for film applications. It is suggested for applications requiring toughness, clarity, high strength, and for blending with LLDPEList o..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman D4008-F Polyethylene (discontinued **) Polyethylene D4008-F is a fractional melt formulation designed for film applications. It is suggested for applications requiring toughness and clarityList of Applications: Food packagingFood-contac..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman E6838-969F Polyethylene (discontinued **) E6838-969F is a low density formulation with no slip and medium antiblock. It is suggested for film applications that require toughness such as shrink/bundling film, disposable diapersand overwrap...
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
ExxonMobil Escorene® LD-108 LDPE Packaging Film Resin, High Clarity (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer high clarity film resin with a good balance of toughness, stiffness, and drawdown capability. This resin has good machinability in ba..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	50 µm (2 mil) film; ASTM D882
DuPont Nucrel® 31001 Ethylene-Acrylic Acid Copolymer Resin for Blown and Cast Film 9.5 wt% Acrylic Acid.Nucrel® 31001 is an ethylene-acrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins.F..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ISO 527-3
Total Lumicene® mPE M 4040 Metallocene Polyethylene, Cast Film Lumicene® mPE M 4040 is a Lumicene® metallocene based Polyethylene with hexene as comonomer.Lumicene® mPE M 4040 can be processed at high output rates with low extrusion pressure, low neck-in, ex..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Huntsman Rexell® L3106 Blown Film Extrusion LLDPE (discontinued **) Linear-low density copolymer, cast film extrusion, FDA compliant.Features: Excellent processability with good sealing and optical properties.Applications: Blending resin and general purpose packagin..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Huntsman Rexell® V3101 Blown Film Extrusion LLDPE (discontinued **) Linear-low very low density copolymer, cast film extrusion, FDA compliant.Features: High toughness, puncture resistance with good sealing and excellent optical properties.Applications: Food packagin..
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Iran Petrochemical (PCC) Arak 0640AA LLDPE (discontinued **) Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, MD	>= 33.0 MPa	>= 4790 psi	ISO 1184
Iran Petrochemical (PCC) Tabriz 0640AA LLDPE (discontinued **) Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman D4052-F Polyethylene (discontinued **) D4052-F is a fractional-melt low density formulation with low slip and low antiblock. It is suggested for film applications requiring impact strength, outstanding clarity, and good tear resistance...
Film Tensile Strength at Break, MD	33.0 MPa	4790 psi	ASTM D882
Eastman E6838-975F Polyethylene (discontinued **) E6838-975F is a low density formulation with medium slip and medium antiblock. The formula is used in general purpose packaging where impact strength and processability are important. End-use film..