Mytex Polymers AS33K(W)-02 Polypropylene, Talc filled, Compounded

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer Mytex Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mytex Polymers AS33K(W)-02 Polypropylene, Talc filled, Compounded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Talc filled compounded polypropylene produced for automotive interior applications using Mytex® Technology.Key Applications: General purpose interiorInformation provided by Mytex Polymers
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
LAB 024
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
Melt Flow 24 g/10 min
24 g/10 min
LAB 012
Ash 20 %
20 %
LAB 025
Mechanical Properties Metric English Comments
Hardness, Rockwell R 96.3
96.3
ISO 2309-2
Hardness, Shore D 66.7
66.7
15 sec; ISO 868
82
82
Instant; ISO 868
Tensile Strength at Break 22.8 MPa
3310 psi
ISO 527
Tensile Strength, Yield 28.6 MPa
4150 psi
50 mm/min; ISO 527
Elongation at Break 15.7 %
15.7 %
ISO 527
Elongation at Yield 3.3 %
3.3 %
ISO 527
Flexural Strength 44.9 MPa
6510 psi
Max load; ISO 178
Flexural Modulus 2.63 GPa
381 ksi
Tangent; ISO 178
2.64 GPa
383 ksi
Chord; ISO 178
Flexural Modulus, 1% Secant 2270 MPa
329000 psi
ISO 178
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
ISO 180
3.40 kJ/m²

@Temperature 23.0 °C
1.62 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact, Notched 0.200 J/cm²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
ISO 178
0.320 J/cm²

@Temperature 23.0 °C
1.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179 / 1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 120 °C
248 °F
ISO 75-1
Deflection Temperature at 1.8 MPa (264 psi) 66.7 °C
152 °F
ISO 75-1