Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D-955
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D-785
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Flexural Yield Strength 56.39 MPa

@Thickness 6.40 mm
8178 psi

@Thickness 0.252 in
ASTM D-790
Flexural Modulus 2.01 GPa

@Thickness 6.40 mm
292 ksi

@Thickness 0.252 in
ASTM D-790
Izod Impact, Notched 3.4314 J/cm

@Thickness 6.40 mm
6.4284 ft-lb/in

@Thickness 0.252 in
ASTM D-256
4.4118 J/cm

@Thickness 3.20 mm
8.2651 ft-lb/in

@Thickness 0.126 in
ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 103 °C
217 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
UL-94