Multibase Multi-Flex® D 3804 TPE Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name Multi-Flex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Flex® D 3804 TPE Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good PaintableForms:PelletsProcessing Method:Injection Molding Information provided by Multibase
Physical Properties Metric English Comments
Specific Gravity 0.960 g/cc
0.960 g/cc
ASTM 792
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 45
45
10 seconds; ASTM D2240
Tensile Strength, Ultimate 13.4 MPa
1950 psi
ASTM D638
Elongation at Break 650 %
650 %
ASTM D638
Flexural Modulus 0.241 GPa
35.0 ksi
1% Secant; ASTM D790
Tear Strength 59.6 kN/m
340 pli
ASTM D624
Thermal Properties Metric English Comments
Brittleness Temperature -50.0 °C
-58.0 °F
ASTM D746
Flame Spread 18 mm/min
0.71 in/min
FM VSS-302
Processing Properties Metric English Comments
Middle Barrel Temperature 210 °C
410 °F
Front Barrel Temperature 227 °C
440 °F
Nozzle Temperature 235 °C
455 °F
Mold Temperature 51.7 °C
125 °F
Drying Temperature 51.7 °C
125 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 3.45 - 4.83 MPa
500 - 700 psi
Back Pressure 0.345 MPa
50.0 psi
Screw Speed 40 rpm
40 rpm
Descriptive Properties Value Comments
Clamp Tonnage 1.5-2.5 tons/in2
Fogging Min. 90
SAE-J275
Injection Rate Fast
Suggested Max Regrind 0.5