Lubrizol Estane® 2103-80AEN Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2103-80AEN Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: NSF Standard 61 certified, FDA complianceAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.00 - 0.0060 cm/cm
0.00 - 0.0060 in/in
ASTM D955
Melt Flow 20 g/10 min

@Load 8.70 kg,
Temperature 224 °C
20 g/10 min

@Load 19.2 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 83
83
ASTM D2240
Tensile Strength, Ultimate 28.9 MPa
4190 psi
ASTM D412
Elongation at Break 650 %
650 %
ASTM D412
50% Modulus 0.00380 GPa
0.551 ksi
ASTM D412
100% Modulus 0.00600 GPa
0.870 ksi
ASTM D412
300% Modulus 0.0110 GPa
1.60 ksi
ASTM D412
Tear Strength 87.6 kN/m
500 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 20
20
H22 Wheel, 1000g; ASTM D1044
Compression Set 30 %
30 %
23°C.
75 %

@Temperature 70.0 °C
75 %

@Temperature 158 °F
30 %

@Temperature 25.0 °C,
Time 79200 sec
30 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
75 %

@Temperature 70.0 °C,
Time 79200 sec
75 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 40 %
40 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 171 µm/m-°C

@Temperature 20.0 °C
95.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 72.0 °C
162 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -45.0 °C
-49.0 °F
Processing Properties Metric English Comments
Melt Temperature 182 - 199 °C
360 - 390 °F
Extrusion
188 - 204 °C
370 - 399 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 82.0 - 93.0 °C
180 - 199 °F
air dew point <-40°C