Lehmann & Voss LUVOCOM® 1105-7041 PEEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7041 PEEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.High chemical resistance parts, hydrolysis resistance, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00060 - 0.0030 cm/cm | 0.00060 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 245 MPa | 35500 psi | |
| Elongation at Yield | 1.4 % | 1.4 % | |
| 1.8 % | 1.8 % | flexural | |
| Modulus of Elasticity | 30.0 GPa | 4350 ksi | |
| Flexural Strength | 355 MPa | 51500 psi | |
| Flexural Modulus | 26.0 GPa | 3770 ksi | |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.00 µm/m-°C | 3.89 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.650 W/m-K | 4.51 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Vicat Softening Point | 320 °C | 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Plansee MW20 Molybdenum-Tungsten
- PolyOne Edgetek® PC-15CF-15GF/000 Polycarbonate (PC)
- Polimeri Europa Eraclene® MM 74 High Density Polyethylene - Injection Molding
- Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced
- Lord Adhesives 7000 Medium Setting, Medium Viscosity, Moisture Resistant Methyl Cyanoacrylate Adhesive
- A. Schulman SCHULAFLEX® SF 302 Ethylene-Based Butene Plastomer
- Hexcel® HexPly® F185 Epoxy Resin, K285 Kevlar Fabric
- Elastocon TPE Technologies Elastocon® STK40 Thermoplastic Elastomer
- Aleris Weldural Aluminum Alloy, 400 mm Thickness
- BASF Neopolen® P 9235 0.04 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved