Hexcel® HexPly® F185 Epoxy Resin, K285 Kevlar Fabric
| Category | Polymer , Thermoset , Epoxy , Epoxy Cure Resin |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F185 Epoxy Resin, K285 Kevlar Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: 285-38"-F185; Fiber: Kev. 49 1140Information provided by HexCel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | 0.40 - 1.2 % | 0.40 - 1.2 % | Prepreg |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 419 MPa @Temperature 24.0 °C |
60800 psi @Temperature 75.2 °F |
Fill TS |
| 507 MPa @Temperature 24.0 °C |
73500 psi @Temperature 75.2 °F |
Warp TS | |
| Tensile Modulus | 24.0 GPa @Temperature 24.0 °C |
3480 ksi @Temperature 75.2 °F |
Warp tensile modulus |
| 26.3 GPa @Temperature 24.0 °C |
3810 ksi @Temperature 75.2 °F |
Fill tensile modulus | |
| Compressive Yield Strength | 155 MPa @Temperature 24.0 °C |
22500 psi @Temperature 75.2 °F |
Warp compression |
| 164 MPa @Temperature 24.0 °C |
23800 psi @Temperature 75.2 °F |
Fill compression | |
| Compressive Modulus | 13.8 GPa @Temperature 24.0 °C |
2000 ksi @Temperature 75.2 °F |
Fill compression |
| 19.3 GPa @Temperature 24.0 °C |
2800 ksi @Temperature 75.2 °F |
Warp compression | |
| Shear Strength | 36.0 MPa @Temperature 24.0 °C |
5220 psi @Temperature 75.2 °F |
Warp short beam shear |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.028 | Laminate |
| Fiber Volume (%) | 42 | Laminate |
| Flow (%) | 24-34 | |
| Wet Resin Content (%) | 52-58 | Prepreg |
Users viewing this material also viewed the following:
- MarkeTech Yttrium aluminum perovskite:Cerium (YAP:Ce; YAlO3) Scintillator Crystal
- LG Chemical LUCEL WK-320 Wear Resistant POM, 20% Mineral Filled, High Modulus
- Lubriplate DS-ES Electric Switch Lubricant Specialty Lubricant and Grease
- Karina 807-10/236-H-Ise White PVC Compound
- Dow Corning XIAMETER® PMCPPMX-200 20Cs Silicone Fluid
- ChevronTexaco FM NLGI 2 Grease EP
- Fainplast Compounds PMP 202 Flexible PVC, Extrusion Modified with PU
- Braskem PH 0130 HOMO Polypropylene Homopolymer
- Plaslok 5314 Black (COM) Impact Grade Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved