Lanxess Pocan® BF 4232 HR 901510 PBT, 30% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Pocan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® BF 4232 HR 901510 PBT, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 30% glass fiber, injection molding, flame retardant, hydrolysis stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Density 1.67 g/cc
0.0603 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 26.72 g/10 min

@Load 2.16 kg,
Temperature 260 °C
26.72 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527-1,-2
Tensile Modulus 9.80 GPa
1420 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 185 MPa
26800 psi
2 mm/min; ISO 178-A
Flexural Modulus 10.0 GPa
1450 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1U
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
16.7 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
55.6 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Melting Point 225 °C
437 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1,-2
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Oxygen Index 36.4 %
36.4 %
Method A; ISO 4589-2
Glow Wire Test 725 °C

@Thickness 1.50 mm
1340 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
1340 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 0.800 mm
1560 °F

@Thickness 0.0315 in
GWIT; IEC 60695-2-13
900 °C

@Thickness 0.400 mm
1650 °F

@Thickness 0.0157 in
GWIT; IEC 60695-2-13
960 °C

@Thickness 0.400 mm
1760 °F

@Thickness 0.0157 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
0.100 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, 60x60x2; ISO 294-4
0.100 %

@Temperature 120 °C,
Time 14400 sec
0.100 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, transverse, 60x60x2; ISO 294-4
Electrical Properties Metric English Comments
Dielectric Strength 29.8 kV/mm
757 kV/in
IEC 60243-1
Comparative Tracking Index 175 - 250 V
175 - 250 V
Solution A; UL 746A
225 V
225 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 4.00 - 8.00 hour

@Temperature 120 °C
4.00 - 8.00 hour

@Temperature 248 °F
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
Karl Fischer test