- LG Chemical Lupox® SG5300 PBT+PET+GF30%
LG Chemical Lupox® SG5300 PBT+PET+GF30%
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® SG5300 PBT+PET+GF30%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PET+GF30%, Good Surface Application: E&E, Automotive (Switch)CAS No. 65997-17-3, 24968-12-5 and 25038-59-9Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm |
0.0040 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 181 MPa @Thickness 3.20 mm |
26300 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.85 GPa @Thickness 3.20 mm |
1140 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.735 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.38 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 6.40 mm |
401 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness >=1.50 mm |
167 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Qualchem Danamid AFGF-20 Polyamide 66, 20% Glass Fiber
- PTS Tristar® PC-10R-CL 10 MFI Clear Polycarbonate with Release
- PolyOne Edgetek® ET3500-5001 colored Acrylonitrile Styrene Acrylate + PC (ASA+PC)
- GrafTech GRAFOIL® GHH Standard Internal Combustion Laminate, Metal Reinforced
- Intercontinental Polymers CoPET 159 CoPET Polymer Type - Clear, Low Melt Polyester Pellets
- Solvay Specialty Polymers Algoflon® F 7 Polytetrafluoroethylene (PTFE)
- Dynasol Calprene® H6170 Hydrogenated Rubber SEBS
- Arlon 55276B028 0.0295" (0.749 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Hexcel® HexWeb® CR III 3/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved