PolyOne Syncure™ System S112FH Polyethylene, Crosslinked (XLPE)
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Syncure™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Syncure™ System S112FH Polyethylene, Crosslinked (XLPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Syncure™ systems are two part moisture crosslinkable compounds. S112FH is an economical flame resistant building wire insulation. Available in RoHS compliant version.NOTE: The above represents Typical Properties measured on 14 AWG with 30 mil wall. STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Deformation | 10 % @Temperature 131 °C, Time 3600 sec |
10 % @Temperature 268 °F, Time 1.00 hour |
500 g; UL 1581 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
| Elongation at Break | 430 % | 430 % | Type IV, 510 mm/min; ASTM D638 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.45 @Frequency 1000 Hz |
2.45 @Frequency 1000 Hz |
ASTM D150 |
| Dissipation Factor | 0.0040 @Frequency 1000 Hz |
0.0040 @Frequency 1000 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Catalyst Masterbatch | 17% | V-0030G RoHS |
| Flame Test | Pass | CSA FT-2; Horizontal |
| Pass | UL 1581; Horizontal | |
| Forms | Pellets | |
| Gel Content | 68% | ASTM D2765; Crosslinked PE, Method B (NonReferee Test) |
| Generic Material | XLPE | |
| Generic Name | Polyethylene, Crosslinked (XLPE) | |
| Grafted Base Resin | 83% | S-1054A |
| Processing Method | Extrusion Coating | |
| Regional Availability | North America | |
| Retention of Tensile Elongation | 90% | 121°C, 1.91 mm; 336 hr, UL Standard |
| Retention of Tensile Strength | 95% | 121°C, 1.91 mm; 336 hr, UL Standard |
| Uses | Building Wire Insulation | |
| Wire & Cable Applications | ||
| Wire Types | NMD90 |