LG Chemical LUPOY EF5001RFT PC/ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY EF5001RFT PC/ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EU Eco-Label compliantApplication: Display housingCAS: 103598-77-2, 9003-56-9 and 125997-21-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Maximum Moisture Content 0.040
0.040
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 56.9 MPa

@Thickness 3.20 mm
8250 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
30 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 93.2 MPa

@Thickness 3.20 mm
13500 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 2.45 GPa

@Thickness 3.20 mm
356 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched >= 4.90 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
>= 9.18 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 94.0 °C

@Thickness 6.40 mm
201 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
140 °F
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL RTI, Mechanical without Impact 60.0 °C
140 °F
Flammability, UL94 V-0

@Thickness >=1.60 mm
V-0

@Thickness >=0.0630 in
V-0

@Thickness >=3.20 mm
V-0

@Thickness >=0.126 in
Processing Properties Metric English Comments
Rear Barrel Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Middle Barrel Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Front Barrel Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Nozzle Temperature 230 - 250 °C
446 - 482 °F
Injection Molding
Melt Temperature 240 - 260 °C
464 - 500 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding