LG Chemical LUPOS GP2300 ABS+GF30%, General Purpose
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS GP2300 ABS+GF30%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, ABS+GF30%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-54-7, 9003-56-9 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 250 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 142 MPa @Thickness 3.20 mm |
20600 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 7.35 GPa @Thickness 3.20 mm |
1070 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.47 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 235 °C | 428 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Nozzle Temperature | 230 - 245 °C | 446 - 473 °F | Injection Molding |
| Melt Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA6 G - G - at 50% RH
- Petroquimica Triunfo Trithene® TS 7001 LDPE - Heavy Duty Low Friction Film
- Huntsman Araldite GT 6259 Bisphenol A Epoxy Solid Resin
- Lucent Polymers GPP-330 Polypropylene, 30% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- Spartech PP5440 Glass Fiber Reinforced Homopolymer
- Techmer ES Luriblend® PA6/6 AF10 HS L Nylon 66
- Fainplast Compounds HGK 84 Flexible PVC, Sheathing for High Temperatures Lead Free
- 3M 7242 HP Indigo Optimized Polyester Label Product
- Carpenter Extendo-Die® Hot Work Die Steel, Tempered 593°C
- SABIC Innovative Plastics LNP Verton RX93407D PA 66 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved