LG Chemical LUMID HI5001AS PA6/PO, High Barrier Property, CaCl2 Resistance, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI5001AS PA6/PO, High Barrier Property, CaCl2 Resistance, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6/PO, High Barrier Property, CaCl2 Resistance, High ImpactApplication: Automotive (Fuel System Tube)CAS No. 25038-54-4, 9010-79-1, 9002-88-4 and 105-60-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Temperature 23.0 °C, Time 86400 sec |
0.50 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.7 MPa @Thickness 3.20 mm |
6040 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 330 % @Thickness 3.20 mm |
330 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 20.1 MPa @Thickness 6.40 mm |
2920 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 0.481 GPa @Thickness 6.40 mm |
69.7 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
2.57 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |