LG Chemical AF360S ABS, TBBA-free Flame Retardant, Low Flow

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical AF360S ABS, TBBA-free Flame Retardant, Low Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, TBBA-free Flame Retardant, Low FlowApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 84852-53-9 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Extrusion Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 6.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 99
99
ASTM D785
Tensile Strength, Yield 42.2 MPa

@Thickness 3.20 mm
 6120 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %

@Thickness 3.20 mm
 >= 5.0 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Tensile Modulus 2.16 GPa

@Thickness 3.20 mm
 313 ksi

@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 66.7 MPa

@Thickness 6.40 mm
 9670 psi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 6.40 mm
 341 ksi

@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 1.77 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 3.31 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
2.45 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.59 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.686 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 1.29 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.785 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 6.40 mm
 203 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 6.40 mm
 185 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 94.0 °C

@Load 5.00 kg
 201 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
 V-0

@Thickness >=0.0787 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Processing Properties Metric English Comments
Zone 1 170 - 190 °C
338 - 374 °F
Extrusion Molding
Zone 2 180 - 200 °C
356 - 392 °F
Extrusion Molding
Zone 3 200 - 220 °C
392 - 428 °F
Extrusion Molding
Zone 4 200 - 220 °C
392 - 428 °F
Extrusion Molding
Adapter Temperature 200 - 230 °C
392 - 446 °F
Extrusion Molding
Die Temperature 200 - 230 °C
392 - 446 °F
Extrusion Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Extrusion Molding
Roll Temperature 60.0 - 90.0 °C
140 - 194 °F
Bottom, Extrusion
70.0 - 90.0 °C
158 - 194 °F
Middle, Extrusion
70.0 - 100 °C
158 - 212 °F
Top, Extrusion
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Extrusion Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Extrusion Molding