LATI Latigloss 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled
Manufacturer LATI
Trade Name Latigloss
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latigloss 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Polyamide 66 (PA66). Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0085 cm/cm
0.0060 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa

@Temperature 150 °C
10900 psi

@Temperature 302 °F
100 MPa

@Temperature 120 °C
14500 psi

@Temperature 248 °F
130 MPa

@Temperature 90.0 °C
18900 psi

@Temperature 194 °F
180 MPa

@Temperature 60.0 °C
26100 psi

@Temperature 140 °F
235 MPa

@Temperature 23.0 °C
34100 psi

@Temperature 73.4 °F
Elongation at Break 2.2 %

@Temperature 23.0 °C
2.2 %

@Temperature 73.4 °F
2.6 %

@Temperature 60.0 °C
2.6 %

@Temperature 140 °F
5.7 %

@Temperature 90.0 °C
5.7 %

@Temperature 194 °F
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
7.5 %

@Temperature 150 °C
7.5 %

@Temperature 302 °F
Tensile Modulus 5.80 GPa

@Temperature 150 °C
841 ksi

@Temperature 302 °F
6.60 GPa

@Temperature 120 °C
957 ksi

@Temperature 248 °F
11.0 GPa

@Temperature 90.0 °C
1600 ksi

@Temperature 194 °F
18.0 GPa

@Temperature 60.0 °C
2610 ksi

@Temperature 140 °F
22.5 GPa

@Temperature 23.0 °C
3260 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Vicat Softening Point 240 °C

@Load 5.00 kg
464 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 280 - 320 °C
536 - 608 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa