SABIC Innovative Plastics Valox® 412 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 412 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX 412 is 20% glass reinforced PBT injection moulding resin. Applications: Spotlights, appliance housings and handles.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Filler Content 20 %
20 %
ASTM D229
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.28 %
0.28 %
ISO 62
Viscosity 165000 cP
165000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
Melt Flow 12 g/10 min

@Load 3.80 kg,
Temperature 200 °C
 12 g/10 min

@Load 8.38 lb,
Temperature 392 °F
 ASTM D1238
40 g/10 min

@Load 5.00 kg,
Temperature 266 °C
 40 g/10 min

@Load 11.0 lb,
Temperature 511 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
23 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 23 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
35 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 35 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 132 MPa
19100 psi
ISO 2039-1
Tensile Strength at Break 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
115 MPa
16700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
120 MPa
17400 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
5.0 %
5.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 7.20 GPa
1040 ksi
5 mm/min; ASTM D638
7.20 GPa
1040 ksi
1 mm/min; ISO 527
Flexural Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
170 MPa
24700 psi
2 mm/min; ISO 178
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
170 MPa
24700 psi
2 mm/min; ISO 178
Flexural Modulus 5.80 GPa
841 ksi
1.3 mm/min, 50 mm span; ASTM D790
5.90 GPa
856 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
0.750 J/cm

@Temperature -30.0 °C
 1.41 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
0.800 J/cm

@Temperature 0.000 °C
 1.50 ft-lb/in

@Temperature 32.0 °F
 ASTM D256
Izod Impact, Unnotched 7.30 J/cm
13.7 ft-lb/in
ASTM D4812
6.50 J/cm

@Temperature -30.0 °C
 12.2 ft-lb/in

@Temperature -22.0 °F
 ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature 0.000 °C
 3.33 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/2C
5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.800 J/cm²
3.81 ft-lb/in²
ISO 179/2C
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/2C
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
 40.6 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
 3.1

@Frequency 1.00e+6 Hz
 IEC 60250
3.3

@Frequency 50.0 - 60.0 Hz
 3.3

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
24.0 kV/mm

@Thickness 1.60 mm
 610 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
26.0 kV/mm

@Thickness 0.800 mm
 660 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
26.0 kV/mm

@Thickness 0.800 mm
 660 kV/in

@Thickness 0.0315 in
 in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 300 V
300 V
IEC 60112
250 - 400 V
250 - 400 V
UL 746A