- Polymer Property : Maximum Service Temperature, Air = 203 °F
Polymer Property : Maximum Service Temperature, Air = 203 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C. (dry sample) |
| Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | short period, no load |
| Omnia Plastica PE 500 - Polyethylene 500 Polyethylene with a molecular weight of ± 500,000. PE 500 is more rigid than the high molecular weight polyethylene and it is therefore more suitable for mechanical applications. The friction coeff.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous; 5,000 h |
| Quadrant EPP Ertalon® 66 SA PA 66, extruded (ISO Data) Material with a higher mechanical strength, stiffness, heat and wear resistance than Ertalon 6 SA. It also has a better creep resistance but its impact strength and mechanical damping ability is red.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous; 5,000 h |
| Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data) The addition of MoS2 renders this material somewhat stiffer, harder and dimensionally more stable than Ertalon 66 SA, but results in some loss of impact strength. The nucleating effect of the molybd.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| PolyOne Bergamid™ B650 G/Mi20 UF Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| PolyOne Bergamid™ B650 Mi10 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Maximum Service Temperature, Air | 95.0 - 105 °C | 203 - 221 °F | Softening Range |
| Huntsman Araldite GT 6084 Bisphenol A Epoxy Solid Resin Weight per Epoxide (EEW, g/eq) 875 to 1025. Max color is 1.Comments/Applications: Unmodified bis A "Type 4" epoxy. Specifically designed for esterification reactions to produce epoxy esters for hi.. |
|||
| Maximum Service Temperature, Air | 95.0 - 105 °C | 203 - 221 °F | Softening Range |
| Huntsman Araldite GT 9545 Bisphenol A Epoxy Solid Resin Weight per Epoxide (EEW, g/eq) 875 to 1025. Max color is 1.Comments/Applications: Unmodified bis A "Type 4" epoxy resin. Powder coating version of GT 6084; moderate flow.Data provided by Ciba Spec.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
| Manifattura Cattaneo PA 6.6 Nylon Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
| LATI Latamid 66 B H-V0 PA 66, Heat Stabilized, Flame Retardant Polyamide 66 (PA66) based compound. High fluidity. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Blended with PA6.Availability: Africa & Middle East.. |
|||
| Maximum Service Temperature, Air | 95.0 - 105 °C | 203 - 221 °F | Softening point |
| Mitsui MILEXâ„¢ RN-2830MB Acrylic Rubber Modified Phenolic Resin The MILEXâ„¢ Family of products is widely featured in brake systems of automobiles made by automakers through Mitsui Chemicals'. The phenolic material is primarily used as binders in brake pad.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
| Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
| Zell-Metall Engineering Plastics Zellamid 250 (PA6.6) at 50% RH Zellamid® 250 is noted for its high temperature resistance and high tensile strength. It is the hardest and most rigid type of extruded Nylon. Main characteristics are high resistance to fuels, oil.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
| Zotefoams Plastazote® LD15FM Low Density Polyethylene Foam, Flame Retarded Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Deflection Temperature with load unspecified |
| Trelleborg Sealing Solutions Turcite® TX Self-Lubricating Thermoplastic Rod Red color. Turcite® TX is engineered to handle moderate load, high speed applications. It exhibits an excellent surface finish when machined. It has a long service life and exceptionally low coe.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
| Zotefoams Plastazote® MP24 Metallocene Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
| Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
| Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Wet Service |
| Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
| Maximum Service Temperature, Air | <= 95.0 °C | <= 203 °F | Laundering Resistance |
| EMS-Griltech Griltex® 2A Copolyamide Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | short term; EMS |
| EMS-Grivory Grivory® TR 55 LX PA12/MACMI Product description: Grilamid TR 55 LX natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 55 LX natural offers outstanding prop.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | short term; EMS |
| EMS-Grivory Grivory® TR 90 LXS PAMACM12 Product description: Grilamid TR 90 LXS natural is a high purity transparent thermoplastic polyamide, based on aliphatic and cycloaliphatic monomers. Grilamid TR 90 LXS natural contains a processing.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
| Eurofoam Porocell POR 304 CM-BI EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
| Eurofoam Porocell POR 304 CM-HD EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Permanent |
| 3M ScotchCal™ 3698E Graphic Film Material 3M™ ScotchCal™ Graphic Film Materials 3690E and 3698E are flexible cast vinyl films suitable for conforming to curved and textured surfaces, including most low surface energy plastics and small di.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | |
| Zotefoams Plastazote® LD15 Low Density Polyethylene Foam Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outs.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | short term; EMS |
| EMS-Grivory Grivory® TR 55 LZ PA12/MACMI Product description: Grilamid TR grades are transparent thermoplastic polyamides based on aliphatic and cycloaliphatic blocks. Grilamid TR 55 LZ offers a variety of interesting properties such as: c.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | ASTM D 3575 |
| Eurofoam Porocell POR 304 CM-HD 200 EPDM Foam Ethylene Propylene Diene Monomer Foam. Used for thermal insulation and soundproofing, antivibration and waterproofing; different types of gaskets.Information provided by Eurofoam s.r.l. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Long Term |
| CENTROPLAST CENTROMID 6.6 Polyamide 6.6 This material has good hardness, wear resistance, abrasion strength and impact strength. It is used for bearing cages, sliding bearings and articulated joint blocks.Information provided by CENTROPL.. |
|||
| Maximum Service Temperature, Air | 95.0 °C | 203 °F | Post Cure, Wet Service |
| Chesterton ARC S4+ 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375.. |
|||