LATI Laramid G/30-V0HF1 PPA, 30% Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Laramid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/30-V0HF1 PPA, 30% Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0050 cm/cm
0.0035 - 0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
85.0 MPa

@Temperature 120 °C
 12300 psi

@Temperature 248 °F
100 MPa

@Temperature 90.0 °C
 14500 psi

@Temperature 194 °F
110 MPa

@Temperature 60.0 °C
 16000 psi

@Temperature 140 °F
120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
Elongation at Break 1.3 %

@Temperature 23.0 °C
 1.3 %

@Temperature 73.4 °F
1.5 %

@Temperature 60.0 °C
 1.5 %

@Temperature 140 °F
2.0 %

@Temperature 90.0 °C
 2.0 %

@Temperature 194 °F
4.0 %

@Temperature 120 °C
 4.0 %

@Temperature 248 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
Tensile Modulus 5.00 GPa

@Temperature 150 °C
 725 ksi

@Temperature 302 °F
7.50 GPa

@Temperature 120 °C
 1090 ksi

@Temperature 248 °F
9.00 GPa

@Temperature 90.0 °C
 1310 ksi

@Temperature 194 °F
11.5 GPa

@Temperature 60.0 °C
 1670 ksi

@Temperature 140 °F
13.0 GPa

@Temperature 23.0 °C
 1890 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Glow Wire Test 775 °C

@Thickness 1.00 mm
 1430 °F

@Thickness 0.0394 in
 GWIT
775 °C

@Thickness 2.00 mm
 1430 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: