- Inchem Phenoxy PKFE
Inchem Phenoxy PKFE
| Category | Polymer , Thermoplastic |
| Manufacturer | Inchem |
| Trade Name | Phenoxy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inchem Phenoxy PKFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Phenoxy PKFE - polyhydroxy ether of Bisphenol A. Originally developed by Union Carbide. Produced by InChem Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 0.13 % | 0.13 % | ASTM D570 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | |
| Moisture Vapor Transmission | 1.38 cc-mm/m²-24hr-atm | 3.51 cc-mil/100 in²-24hr-atm | |
| Oxygen Transmission | 2.28 cc-mm/m²-24hr-atm | 5.79 cc-mil/100 in²-24hr-atm | |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | |
| Hardness, Shore D | 75 | 75 | |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | |
| Tensile Strength, Yield | 62.1 MPa | 9010 psi | |
| Elongation at Break | 90 % | 90 % | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| Modulus of Elasticity | 2.62 GPa | 380 ksi | |
| Flexural Yield Strength | 96.6 MPa | 14000 psi | |
| Flexural Modulus | 2.83 GPa | 410 ksi | |
| Compressive Yield Strength | 82.8 MPa | 12000 psi | |
| Compressive Modulus | 2.24 GPa | 325 ksi | |
| Poissons Ratio | 0.38 | 0.38 | |
| Shear Modulus | 0.949 GPa | 138 ksi | Calculated |
| Izod Impact, Notched | 1.31 J/cm | 2.45 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 57.6 µm/m-°C @Temperature -30.0 - 100 °C |
32.0 µin/in-°F @Temperature -22.0 - 212 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.60 | 1.60 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.8 | 3.8 | |
| 4.1 | 4.1 | ||
| Dielectric Strength | 20.5 kV/mm | 521 kV/in | |
| Dissipation Factor | 0.0012 | 0.0012 | |
| 0.030 | 0.030 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 230 °C | 446 °F | |
| Rear Barrel Temperature | 190 °C | 374 °F | |
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 230 °C | 446 °F | |
| Nozzle Temperature | 230 °C | 446 °F | |
| Mold Temperature | 50.0 °C | 122 °F | |
| Drying Temperature | 70.0 °C | 158 °F |
Users viewing this material also viewed the following:
- Fine Organics FINALUX G 111 Lubricant Additive
- Lubrizol Advanced Materials PEARLBOND® 102 Linear Thermoplastic Polyurethane
- Sharadaa Ceramics Blankets
- SABIC Innovative Plastics LNP STAT-KON PX93058 PA 6 (Europe-Africa-Middle East)
- A. Schulman FORMION™ FI 330 Ionomer
- TIMCAL TIMREX® KS44 Primary Synthetic Graphite
- Adell AH-38 Nylon 66, 40% Mineral Filled
- Bhansali Engineering Santron IMS1000 Sparkle SAN Resin
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 65A
Copyright © lookpolymers.com All Rights Reserved