Polymer Property : Dielectric Strength = 521 kV/in Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Strength	20.5 kV/mm	521 kV/in
Inchem Phenoxy PKFE Phenoxy PKFE - polyhydroxy ether of Bisphenol A. Originally developed by Union Carbide. Produced by InChem Corporation.
Dielectric Strength	20.5 kV/mm	521 kV/in
Momentive Performance Materials RTV511 Silicone Rubber Compound for Low Temperature Potting, Encapsulating and Sealing, White RTV511, RTV560 and RTV577 silicone rubber compounds are low temperature two-part silicone elastomers. They are supplied ready to use with a base compound and DEBT (deputy tin deflagrate) as the stan..
Dielectric Strength	20.5 kV/mm @Thickness 1.90 mm	521 kV/in @Thickness 0.0748 in
Momentive Performance Materials RTV511 White Extreme Low Temperature Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6126 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6136 Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6156 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6166 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6186 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 1.91 mm	521 kV/in @Thickness 0.0750 in
Momentive Performance Materials RTV6196 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Dielectric Strength	20.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C	521 kV/in @Thickness 0.126 in, Temperature 73.4 °F	DAM; Short Time; ASTM D149
DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612 Zytel® 77G33HS1L NC010 is a 33% glass fiber reinforced, heat stabilized polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers