Fiberfil® J-60/20/H Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer FiberFil
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fiberfil® J-60/20/H Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by FIBERFIL Engineered Plastics
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Water Absorption 0.030 %
0.030 %
24 hr; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm

@Thickness 3.17 mm
0.0030 in/in

@Thickness 0.125 in
ASTM D955
0.0040 cm/cm

@Thickness 6.35 mm
0.0040 in/in

@Thickness 0.250 in
ASTM D955
Melt Flow 5.0 g/10 min
5.0 g/10 min
230/2.16 (typical); ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100 - 110
100 - 110
ASTM D785
Tensile Strength, Yield 68.9 MPa
10000 psi
ASTM D638
Elongation at Yield 3.5 %
3.5 %
ASTM D638
Tensile Modulus 4.14 GPa
600 ksi
ASTM D638
Flexural Strength 93.1 MPa
13500 psi
ASTM D790
Flexural Modulus 3.79 GPa
550 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 157 °C
315 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 210 °C
390 - 410 °F
Middle Barrel Temperature 204 - 227 °C
400 - 440 °F
Front Barrel Temperature 182 - 199 °C
360 - 390 °F
Nozzle Temperature 182 - 193 °C
360 - 380 °F
Melt Temperature 199 - 232 °C
390 - 450 °F
Mold Temperature 32.2 - 71.1 °C
90.0 - 160 °F
Drying Temperature 76.7 °C
170 °F
Drying not normally required
Dry Time 2 hour
2 hour
Drying not normally required
Moisture Content <= 0.20 %
<= 0.20 %
recommended for molding
Back Pressure 0.000 - 0.689 MPa
0.000 - 100 psi