Hippe PVC-U Polyvinyl Chloride
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe PVC-U Polyvinyl Chloride.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Material at reasonable price, high strength. Used in machine construction as covers, pipes, section, façade elements.Information provided by Hippe.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | DIN 53 479 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa @Time 30.0 sec |
14500 psi @Time 0.00833 hour |
DIN 53 456 |
| Tensile Strength | 50.0 MPa | 7250 psi | DIN 53 455 |
| Elongation at Break | 10 % | 10 % | DIN 53 455 |
| Tensile Modulus | 1.70 GPa | 247 ksi | DIN 53 457 |
| Flexural Modulus | 2.80 GPa | 406 ksi | from bending test; DIN 53 457 |
| Charpy Impact, Notched | NB | NB | DIN 53 453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C | 38.9 - 44.4 µin/in-°F | |
| Specific Heat Capacity | 0.850 - 0.900 J/g-°C | 0.203 - 0.215 BTU/lb-°F | |
| Thermal Conductivity | 0.140 - 0.170 W/m-K | 0.972 - 1.18 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | Continuous use |
| 100 °C | 212 °F | Short Periods | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO-R 75 Method A |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DIN 53 482, VDE 0303, Part 3 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53 482 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
DIN 53 483, IEC-250 |
| Dielectric Strength | >= 35.0 kV/mm | >= 889 kV/in | Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1 |
| Dielectric Loss Index | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
DIN 53 483, IEC-250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | transp. Opaque black, red/gray | |
| Creep Resistance | Grade CTI 600 | DIN 53 480, IEC-112, VDE 0303 Part 1 |
Users viewing this material also viewed the following:
- Polimeri Europa KOBLEND PCA PD 54 PC+ABS (discontinued **)
- Honeywell Aegis™ HCA155QP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- Loxim 315 01HB Nylon 6
- Kaneka PHBH Rigid Bio-based Polymer
- A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
- ChevronTexaco Aquagear® EP 220
- Entec Hypro™ PPC-T20 Copolymer Polypropylene, 20% Talc Reinforced
- Chosun Refractories COD-1 Special brick
- Aclo Accutech Polypropylene Homopolymer HP0339G20CL Glass Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved