Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.70 GPa | 247 ksi | STN EN ISO 527-2 |
Plastcom SLOVALEN PC 51 C 30 Polypropylene Homopolymer and Copolymer, 30% Micronized Talc FeaturesModified homopolymer and copolymer PP for injection moulding with the content of 30% micronized, chemically modified talc. Increased strength, rigidity and thermal application up to 120°C... |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | |
Plastcom SLOVALEN PH 59 GB 20 PP, 20% glass beads, mod. of mech. prop. FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
NCMT NanoPAC™ S206 High Performance Polypropylene Nanocomposite Characteristics: High stiffness Supplementary of ABS Good impact resistant Less shrinkage Good thermal conductivity Applications: Toys Industry AutomobileInformation provided by Nano Composite Mater.. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers Optrene 10GF Polypropylene Chemically coupled glass reinforced(10%) polypropylene with high strength and HDT.Information provided by Ovation Polymers |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers OPTRENE 10GF Polypropylene, 10% Glass Reinforced Properties of chemically coupled glass reinforced (10 %) polypropylene with high strength and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
Shell Carilon® DA6L1A10 Polyketone, Lubricated Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DA6L1A10 is a lubricated injection molding grade with mechanical properties which classify it as an.. |
|||
Tensile Modulus | 1.70 - 2.50 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
247 - 363 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 6010 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6010 PVDF homopolymer has medium viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
Ineos ABS Lustran® 552 Extrusion, Profile/Substrate Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
Lanxess Pocan® S 1506 000000 PBT PBT, non-reinforced, injection molding extrusion, impact modified |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ASTM D638 |
Ineos ABS Triax® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON CX99000 PS (Europe-Africa-Middle East) LNP* STAT-KON* CX99000 is a compound based on Polystyrene containing Carbon Powder. Added features include : Electrically Conductive, Easy Molding. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X6800BM PBT (Asia Pacific) Blow moldable, impact modifed XENOY |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
Styrolution Terluran® SP-6 ABS Description: High impact grade, suitable for extrusion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
Suzhou Hipro Polymers Hiprolon® 90 NN Nylon 612, condition Hiprolon® 90 NN is medium viscosity polyamide 6.12. Features: low density, low water absorption, high dimension stability, high impact and notched impact resistance, good chemical resistance and .. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EE168AI Polypropylene TPO Compound Daplen™ EE168AI is a 10% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. .. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
Borealis HB300TF Polypropylene HB300TF is a polypropylene homopolymer intended for thermoformed packaging applications. This grade is produced using the Borealis nucleating technology. Its increased crystallization temperature a.. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-2 |
Total PPH 11012 Polypropylene Homopolymer, Injection Molding Polypropylene PPH 11012 is a nucleated controlled-rheology antistatic homopolymer with a high melt flow index of 55 g/10 min.Polypropylene PPH 11012 is characterized by high fluidity for high speed .. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
Borealis Daplen™ EF261AI Polypropylene TPO Compound Daplen™ EF261AI is a 20 % mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process... |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ASTM-D790 |
Polyram RamShine PS503 Polystyrene, Flame Retardant Flame retardant, high impact polystyrene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527 |
CP-Polymer-Technik Wellamid® 6600 GS 15 HWCP 15% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4129 black 9020 PA610 Product description: Grilamid XE 4129 black 9020 is a high viscosity Polyamide 610 especially suitable for extrusion applications. A characteristic of tubes made out of this material is the high res.. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
Eurostar Starglas FF001 HDPE, Glass Fiber Filled Starglas FF001 is a Glass Fiber Reinforced High Density Polyethylene ResinInformation provided by Eurostar. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | |
BASF Polystyrol® 473 D Impact Grade Polystyrene (Europe) Easy flowing, high-impact grade, often blended with easy flowing general purpose Polystyrol; easy to thermoform.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned) Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF |
|||
Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min |
Arkema Group Oroglas® SG 10 Acrylic, Gamma Radiation Resistant
(discontinued **) OROGLAS SG 10 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no advers.. |