Gouda Vuurvast CURAS 90 SPF Moldable Refractory Material

Category	Ceramic , Oxide , Aluminum Oxide
Manufacturer	Gouda Vuurvast
Trade Name	CURAS
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Gouda Vuurvast CURAS 90 SPF Moldable Refractory Material.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Curas 90 S PF is a moldable which is characterized by its outstanding abrasion resistance (acc. to ASTM C-704: < 3 cc). This material is supplied as a powder which only has to be mixed with potable water to the required consistency. Curas 90 S PF is applied, for example, in FCC units. It can be installed very efficiently, instructions for use are available.Information provided by Gouda Vuurvast.

Physical Properties	Metric	English	Comments
Bulk Density	2.70 - 2.80 g/cc	0.0975 - 0.101 lb/inÂ³	After drying at 110Â°C

Mechanical Properties	Metric	English	Comments
Compressive Strength	115 - 125 MPa @Temperature 100 Â°C	16700 - 18100 psi @Temperature 212 Â°F	Cold Crushing Strength
	150 - 170 MPa @Temperature 1300 Â°C	21800 - 24700 psi @Temperature 2370 Â°F	Cold Crushing Strength

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.850 - 0.950 W/m-K @Temperature 100 Â°C	5.90 - 6.59 BTU-in/hr-ftÂ²-Â°F @Temperature 212 Â°F
	0.930 - 1.13 W/m-K @Temperature 600 Â°C	6.45 - 7.84 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
	1.23 - 1.43 W/m-K @Temperature 1300 Â°C	8.54 - 9.92 BTU-in/hr-ftÂ²-Â°F @Temperature 2370 Â°F
Maximum Service Temperature, Air	1600 Â°C	2910 Â°F
Shrinkage	-0.200 - 0.200 % @Temperature 1300 Â°C	-0.200 - 0.200 % @Temperature 2370 Â°F	Permanent Linear Change

Component Elements Properties	Metric	English
Al2O3	82 %	82 %
P2O5	1.0 %	1.0 %
SiO2	13 %	13 %
TiO2	2.0 %	2.0 %

Descriptive Properties	Value	Comments
Bonding Type	chemical/ceramic
Material Consumption per 1 m3	2700 kg
Mixing Water	4-5.5 liters	per 100 kgs dry material
Segercone	Min 37