FKuR Kunststoff Bio-Flex® F 6611 Compostable PLA Blend

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer FKuR Kunststoff GmbH
Trade Name Bio-Flex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF FKuR Kunststoff Bio-Flex® F 6611 Compostable PLA Blend.pdf
  Online Service   lookpolymers   27660005
Material Notes:
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any starch or starch derivatives. Bioplastics generally replace conventional materials such as low density polyethylene (LDPE), high density polythene (HDPE) as well as polystyrene (PS) and polypropylene (PP). For packaging applications these materials need to be converted into film which is as thin as possible while maintaining high tensile strength. Depending on the specific application, packaging films have to provide a high barrier against humidity, oxygen and aromas or alternatively provide adequate permeability (“breathability”).BIO-FLEX® F 6611 is a certified GMO-free and consistent further development of the current product portfolio. BIO-FLEX® F 6611 is ideally used for thermoforming. It is pleasant to the touch and has a pearlescent gloss. With a heat distortion temperature of over 130 °C, which can be reached by appropriate processing, it has an outstanding heat resistance for a bioplastic. BIO-FLEX® F 6611 is furthermore biodegradable and predominantly composed of renewable resource raw materials. Information Provided by FKuR Kunststoff GmbH
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Melt Flow 4.0 - 6.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.0 - 6.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 16.0 MPa
2320 psi
At break; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
ISO 527
Elongation at Break 9.7 %
9.7 %
ISO 527
Elongation at Yield 2.5 %
2.5 %
ISO 527
Tensile Modulus 2.73 GPa
396 ksi
ISO 527
Flexural Yield Strength 66.0 MPa

@Strain 3.5 %
9570 psi

@Strain 3.5 %
ISO 178
Flexural Modulus 2.51 GPa
364 ksi
ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C

@Temperature 73.4 °F
No Break; ISO 179-1/1eU
Charpy Impact, Notched 0.690 J/cm²

@Temperature 23.0 °C
3.28 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eA
Thermal Properties Metric English Comments
Melting Point 150 - 170 °C
302 - 338 °F
ISO 3146-C
Vicat Softening Point 62.0 °C
144 °F
A; ISO 306
Descriptive Properties Value Comments
Flexural Elongation at break (%) No break
ISO 178
Melt Volume Flow (cm3/10 min) 3.5-5.0
ISO 1133; 190°C, 2.16kg