Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.5 - 6.0 g/10 min | 2.5 - 6.0 g/10 min | ASTM D1238 |
S&E Specialty Polymers GPE2001F-ROHS PVC Application: GPE2001F-ROHS is flame retardant polyethylene compound designed for wire and cable applications. GPE2001F-ROHS complies with RoHS requirements. GPE2001F-ROHS is suitable for 75°C cont.. |
|||
Melt Flow | 1.0 - 6.0 g/10 min | 1.0 - 6.0 g/10 min | ASTM D1238 |
Polymer Resources PC/TP-GP2-G20 PC Polyester, Excellent Chemical Resistance, 20% Glass Filled
(Unverified Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
Kazanorgsintez PC-005 Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for product manufacture by method of extrusion and die-casting.Information Provided by Kazanorgsintez |
|||
Melt Flow | 4.0 - 6.0 g/10 min | 4.0 - 6.0 g/10 min | ASTM D1238 |
Micropol Microlin LL17 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
Melt Flow | 4.0 - 6.0 g/10 min | 4.0 - 6.0 g/10 min | ASTM D1238 |
Micropol Microlin ML27 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
Shanghai Ofluorine 9202F PVDF Powder for cables Description: Excellent mechanical properties, heat resistance and flame resistance, PVDF for cable can bear high temperature, corrosive chemicals etc harsh working environment, which has low smoke, .. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 710 Utility Black ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the manufacturer. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 710H Utility Black ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 720H Black ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 730 Utility White ABS Good impact strength, easy processability, good chemical resistance, good wear and abrasion resistance.Data provided by the Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 730H White ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Shuman 780H Grey ABS Good impact strength, easy processability, good chemical resistanceInformation provided by Shuman Plastics, Inc. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 150 °C |
2.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 302 °F |
|
Taiwan Sheen Soon Sheenthane® AH-571 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for soft hotmelt adhesiveExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized. Used for hot melt adhes.. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 - 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Borcoat™ ME0433 Polyethylene Adhesive In Powder form for Steel Pipe Coating Borcoat ME0433 is a maleic-anhydride grafted polyethylene polymer with excellent adhesion to fusion bonded epoxy and the top-coat HDPE.Borcoat HE0433 is primarily designed to be used as the tie laye.. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Adell YS-10 PC Alloy |
|||
Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C |
4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
3M Dyneon™ PVDF 2066_0002 Fluoroplastic 3M™ Dyneon™ PVDF 2066/0002, a fluoropolymer material, provides an excellent balance of physical properties, processability, surface smoothness, flexibility, and refractive index, allowing for a wi.. |
|||
Melt Flow | 1.5 - 6.0 g/10 min @Load 2.16 kg, Temperature 200 °C |
1.5 - 6.0 g/10 min @Load 4.76 lb, Temperature 392 °F |
ASTM D1238 |
BecauseWeCare BF90 Biodegradable Plastic Biodegradable and compostable product produced from corn and developed to break down within weeks in a compost environment, without leaving any harmful residues in the process. Certified to the vari.. |
|||
Melt Flow | 1.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 232 °C |
1.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 2821-00 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasi.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 21.6 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 301-F Polyvinylidene Fluoride Powder Characteristics: Fine milled, white, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abra.. |
|||
Melt Flow | 3.0 - 6.0 g/10 min | 3.0 - 6.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Melt Flow | 2.0 - 6.0 g/10 min | 2.0 - 6.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-G10 Modified PPO, 10% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 1.0 - 6.0 g/10 min @Load 5.00 kg, Temperature 232 °C |
1.0 - 6.0 g/10 min @Load 11.0 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR FLEX® 2800-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low.. |
|||
Melt Flow | 2.0 - 6.0 g/10 min @Load 21.6 kg, Temperature 232 °C |
2.0 - 6.0 g/10 min @Load 47.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® 201 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan.. |