DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating  (discontinued **)

Category Polymer , Film , Thermoplastic , Ionomer , Ionomer, Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Surlyn® 1652-1 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, seafood and cheese packaging; Cereal liners; Medical/pharmaceutical packaging; Powdered/granular food and nonfood pouches; Edible oil, motor oil, and other liquid product pouches; Snack structuresData provided by the manufacturer, DuPont Packaging.
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ASTM D792
Melt Flow 4.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 400 %
400 %
ASTM D882
Secant Modulus, MD 0.160 GPa
23.2 ksi
ASTM D882
Secant Modulus, TD 0.0450 GPa
6.53 ksi
ASTM D882
Impact 220
220
Spencer Impact in J/cm; ASTM D3420
Elmendorf Tear Strength, MD 3.50 g/micron
88.9 g/mil
Elmendorf Tear Strength, TD 3.70 g/micron
94.0 g/mil
Dart Drop 7.90 g/micron
201 g/mil
ASTM D1709B
Seal Strength <= 2700 g/25 mm
<= 2700 g/in
Varies with seal bar temp.
Hot Tack Strength <= 2000 g/25 mm
<= 2000 g/in
Varies with seal bar temp.; Packforsk Method
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 100 °C
212 °F
DSC; ASTM D3418
Vicat Softening Point 79.0 °C
174 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 3.5 %
3.5 %
ASTM D1003
Gloss 60 %
60 %
20°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 177 °C
351 °F