Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
Polimeri Europa Clearflex® H&T CLH 150 Linear Low Density Polyethylene Clearflex H&T CLH 150 is a linear low density polyethylene resin, with antioxidants, suitable for cast film extrusion.Stretch films obtained from Clearflex H&T CLH 150 show good optical properties, .. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
Polimeri Europa Greenflex® FC 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FC 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FC 45 exhibit good optical properties, excellent impact resistance and low creep.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa @Thickness 0.400 mm |
4350 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1394 Conductive Thermoplastic Compound PRE-ELEC® PP 1394 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
NOVA Chemicals Novapol® GF-0218-F Butene LLDPE Masterbatch Resin Film Properties. Features: Free flowing granules, toughness and strength, ease of extrusion.Applications: Blending, concentrates.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
NOVA Chemicals Novapol® PF-0218-D Butene LLDPE Film Resin Film Properties. Features: High MI for easier extrusion.Applications: Trash bags, bags-on-roll, garment film.Data provided by the manufacturer. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
ExxonMobil Escorene® LD-318 EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-318 exhibits superior impact strength and heat sealability.Applications: Primal meat b.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating
(discontinued **) Surlyn® 1652-1 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylen.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527 |
Metabolix M-vera™ B5010 Film Grade Compostable Bioplastic For use in tough, certified compostable film and bag applications. Mvera B5010 offers a wide range of attractive traits—excellent tear and puncture toughness, excellent seal strength, good prin.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis BD712CF Polypropylene Copolymer BD712CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: BD712CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
Borealis Bormed™ RB801CF Polypropylene Random Copolymer Bormed™ RB801CF is a random copolymer. Applications: Bormed™ RB801CF is intended for packaging for medical devices, pouches, and packaging for pharmaceutical products. Additives: Bormed™ RB801C.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis BorPure™ RD226CF Polypropylene Random Copolymer BorPure™ RD226CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: BorPure™ RD226CF is recommended for food packaging.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis HD204CF Polypropylene HD204CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: HD204CF is recommended for medical applications, inner layer in co extru.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis HD601CF Polypropylene HD601CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: metallisable cast film, inner layer in co extrusion, textile packaging fil.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis HD621CF Polypropylene HD621CF is a polypropylene homopolymer This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. Applications: food packaging, lamination films, statio.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ISO 527-3 |
Borealis Himod™ FT5270 LDPE for Film Himod FT5270 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis BorPURE™ RD208CF Polypropylene Random Copolymer BorPure™ RD208CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. This grade is suitable for the manufacturing of unoriented films o.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis RD735CF Polypropylene Random Copolymer RD735CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD735CF is recommended for food packaging, textile packaging .. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem FM31D LLDPE Blown Film Extrusion Polyethylene Copolymer The FM31D resin is a linear low-density polyethylene, copolymer of butene-1, produced by the solution process for blown film extrusion. It has excellent mechanical properties, especially hot tack. I.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem Green PE SLL218/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Lower greenhouse gas emissions100% made from renewable raw materialsPerformance and Competitiveness: Green Polyethylene has the same characteristics as petrochemical polyethyleneApplications: Line.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem Green PE SLL318 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LD7000A LDPE Blown Film Extrusion Polyethylene LD7000A is a low-density polyethylene produced by the high pressure process in an autoclave reactor. It is developed for the manufacturing of extruded films. It has high mechanical and impact streng.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LF320 LLDPE Cast Film Extrusion Polyethylene Copolymer LF320 is a linear low-density polyethylene, copolymer of butene-1, produced by the gas phase process. It was developed for cast film extrusion. Films obtained with this product show a good processin.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LL318 LLDPE Cast Film Extrusion Polyethylene Copolymer LL318 is a linear low-density polyethylene, copolymer of butene-1, produced by the Spherilene process. It was developed for cast film extrusion. Films obtained with this product show good mechanical.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LL3800N HDPE Cast Film Extrusion Polyethylene Copolymer The resin LL3800N is a high-density polyethylene, copolymer octene-1, produced by the solution process for the extrusion of plain films with excellent mechanical properties. It has an antirust addit.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem TN2005 EVA General Film Copolymer TN2005 is an Ethylene-Vinyl Acetate (EVA) copolymer with high molecular weight, excellent mechanical properties, transparency, high gloss, and easy processing. Additionally, TN2005 has flexibility e.. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
Braskem BF2021 Cast Film Extrusion Low Density Polyethylene Films for diapers and absorbent articles; Medium resistance films or for general use.Information provided by Braskem. |
|||
Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
Braskem LF218/21 LLDPE Cast and Blown Film Extrusion Polyethylene Copolymer LF218/21 is a LLDPE Butene copolymer produced by Braskem. It was specially designed to provide outstanding processing performance. Films obtained with this grade show good physical and optical prope.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 75.8 MPa | 4350 - 11000 psi | Average value: 52.1 MPa Grade Count:28 |
Overview of materials for Linear Low Density Polyethylene (LLDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Blow Molding Grade". Each property range of values reported is .. |
|||
Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
Borealis HD214CF Polypropylene Homopolymer HD214CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: food packaging, lamination films, stationary films, multi layer co-extrus.. |
|||
Film Tensile Strength at Break, MD | 30.0 - 65.0 MPa | 4350 - 9430 psi | Average value: 44.4 MPa Grade Count:5 |
Overview of materials for Polypropylene, Impact Modified; Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Impact Modified; Molded/Extruded". Each property range of values reported is minimum and .. |